| Item | Method | Unit | Flame-resistance type | ||
|---|---|---|---|---|---|
| P50DFR | S2002FB | S2004FS | |||
| Hardness | JIS K6301 | A | 96 | 98 | 98 |
| ASTM D2240 | D | 54 | 57 | 58 | |
| Specific Gravity | ASTM D792 | ? | 1.36 | 1.33 | 1.28 |
| 50% Tensile Modulus | ASTM D638 | MPa | 10.8 | 16.6 | 20.1 |
| 10% Compression Modulus | ASTM D695 | MPa | 9.4 | 15.8 | 19.2 |
| Flexual Modulus | ASTM D790 | MPa | 167 | 230 | 290 |
| Tensile strength | ASTM D638 | MPa | 17.6 | 26.9 | 27.2 |
| Tensile elongation | ASTM D638 | % | 600 | 560 | 550 |
| Tear strength | ASTM D624 | kN/m | 108 | 160 | 155 |
| IZOD notched impact test | ASTM D256 | J/m | NB | NB | NB |
| Taber abrasion | ASTM D1044 | mg/1000c. | 17 | 12 | 12 |
| Resilience | JIS K6301 | % | 65 | 60 | 60 |
| Compression set JIS | JIS K6301 | % | 55 | 65 | 65 |
| Melting point | DSC | ℃ | 215 | 210 | 210 |
| Vicat softening point | ASTM D1525 | ℃ | 170 | 185 | 185 |
| Heat deflection temperature | ASTM D648 | ℃ | 70 | 110 | 110 |
| Brittle point | JIS K6301 | ℃ | < -65 | < -65 | < -65 |
| Flammability | UL94 | ? | V0 | V2 class | V2 class |
| Coefficient of heat expansion | TMA | 1/K | 16×10?? | 13×10?? | 14×10?? |
| Dielectric strength | JIS K2111 | MV/m | 15 | 25 | 30 |
| Volume strength | ASTM D257 | Ω?cm | 6×1013 | 4×1013 | 2×1013 |
| Moisture absorption | 23℃, 65%RH | % | 0.40 | 0.38 | 0.38 |
| Melt flow index | ASTM D1238 | g/10min | 22? | 12? | 12? |
| Mold shrinkage | Mold 2mm thickness | % | 0.8 | 1.3 | 1.3 |
* Melt flow index a:190℃ b:230℃
The data the description is the popular value, not the guaranteed value.
| Item | Method | Unit | High viscous and high durability type | |
|---|---|---|---|---|
| P90BD | P46D-01 | |||
| Hardness | JIS K6301 | A | 96 | 97 |
| ASTM D2240 | D | 57 | 46 | |
| Specific Gravity | ASTM D792 | ? | 1.19 | 1.15 |
| 50% Tensile Modulus | ASTM D638 | MPa | 15.2 | 10.9 |
| 10% Compression Modulus | ASTM D695 | MPa | 13.3 | 9.6 |
| Flexual Modulus | ASTM D790 | MPa | 162 | 110 |
| Tensile strength | ASTM D638 | MPa | 31.4 | 31.9 |
| Tensile elongation | ASTM D638 | % | 700 | 700 |
| Tear strength | ASTM D624 | kN/m | 172 | 165 |
| IZOD notched impact test | ASTM D256 | J/m | NB | NB |
| Taber abrasion | ASTM D1044 | mg/1000c. | 13 | 10 |
| Resilience | JIS K6301 | % | 65 | 70 |
| Compression set JIS | JIS K6301 | % | 57 | 55 |
| Melting point | DSC | ℃ | 203 | 203 |
| Vicat softening point | ASTM D1525 | ℃ | 180 | 153 |
| Heat deflection temperature | ASTM D648 | ℃ | 101 | 74 |
| Brittle point | JIS K6301 | ℃ | < -65 | < -65 |
| Flammability | UL94 | ? | HB class | HB class |
| Coefficient of heat expansion | TMA | 1/K | 14×10?? | 17×10?? |
| Dielectric strength | JIS K2111 | MV/m | 30 | 25 |
| Volume strength | ASTM D257 | Ω?cm | 6×1013 | 4×1013 |
| Moisture absorption | 23℃, 65%RH | % | 0.40 | 0.45 |
| Melt flow index | ASTM D1238 | g/10min | 3? | 0.5? |
| Mold shrinkage | Mold 2mm thickness | % | 1.1 | 0.7 |
* Melt flow index a:190℃ b:230℃
The data the description is the popular value, not the guaranteed value.