特性備注:易流動,易脫模,快速固化 重要參數: 成型收縮率:1.14 % 缺口沖擊強度:10 氧指數:26 % 拉伸強度:50 MPa 斷裂伸長率:35 % 彎曲強度:110 MPa 彎曲模量:2900 MPa
產品說明 | |
Ultramid 8267G HS BK-102 is a heat stabilized, black pigmented, 40% mineral and glass fiber reinforced PA6 injection molding compound. It possesses a balance of engineering properties in combination with excellent dimensional stability, low warp and resistance to sink-mark formation. It exhibits high strength, rigidity, and good heat distortion temperature. It resists creep under load and the heat stabilizer system extends its retention of properties at elevated temperatures. It has good chemical resistance to greases, oils and hydrocarbons. | |
總體 | |
材料狀態 | 已商用:當前有效 |
資料 1 | Processing - Injection Molding (English)Processing - Injection Molding Cooling Times (English)Technical Datasheet - ASTM (English)Technical Datasheet - ISO (English) |
搜索 UL 黃卡 | BASF CorporationUltramid® |
供貨地區 | 北美洲 |
填料/增強材料 | 玻璃纖維增強材料, 15% 填料按重量礦物填料, 25% 填料按重量 |
添加劑 | 熱穩定劑 |
性能特點 | 半結晶尺寸穩定性良好低翹曲性低粘度剛性,良好高強度抗彎曲可加工性,良好良好的表面光潔度良好的抗熱老化性良好的抗蠕變性良好的流動性耐化學性良好耐磨蝕性,良好熱穩定性 |
用途 | 把手草坪和園林設備車輪齒輪動力/其它工具汽車領域的應用:汽車外部零件 |
機構評級 | ULC Unspecified Rating |
RoHS 合規性 | RoHS 合規 |
外觀 | 黑色 |
形式 | 顆粒料 |
加工方法 | 注射成型 |
多點數據 | Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1)Shear Modulus vs. Temperature (ISO 11403-1)Viscosity vs. Shear Rate (ISO 11403-2) |
物理性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
比重 | ||||
-- | 1.48 | -- | ASTM D792 | |
-- | 0.0535 | -- | lb/in3 | ISO 1183 2 |
收縮率 - 流動 (0.125 in) | 0.0040 | -- | in/in | ASTM D955 |
吸水率 | ||||
24 hr | 0.90 | -- | % | ASTM D570 |
73°F, 24 hr | 0.90 | -- | % | ISO 62 |
飽和 | 5.7 | -- | % | ASTM D570, ISO 62 2 |
平衡, 50% RH | 1.6 | -- | % | ASTM D570 |
平衡 | 1.6 | -- | % | ISO 62 2 |
硬度 | 干燥 | 調節后的 | 單位制 | 測試方法 |
洛氏硬度 (R 計秤) | 121 | -- | ASTM D785 | |
球壓硬度 | 31900 | -- | psi | ISO 2039-1 |
機械性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
拉伸模量 | ||||
-40°F | 1.42E+6 | -- | psi | ISO 527-2 |
176°F | 512000 | -- | psi | ISO 527-2 |
250°F | 397000 | -- | psi | ISO 527-2 |
-- | 1.20E+6 | 603000 | psi | ISO 527-2 2 |
抗張強度 | ||||
斷裂, 73°F | 18900 | 9720 | psi | ASTM D638 |
斷裂 | 18100 | 9720 | psi | ISO 527-2 2 |
伸長率 | ||||
斷裂, 73°F | 3.0 | 14 | % | ASTM D638 |
斷裂 | 3.0 | 14 | % | ISO 527-2 2 |
彎曲模量 | ||||
73°F | 1.15E+6 | -- | psi | ASTM D790 |
73°F | 1.04E+6 | 534000 | psi | ISO 178 |
彎曲強度 | ||||
73°F | 31200 | -- | psi | ASTM D790 |
73°F | 28300 | 13100 | psi | ISO 178 |
沖擊性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
簡支梁缺口沖擊強度 | ISO 179/1eA 2 | |||
-22°F | 1.67 | -- | ft·lb/in2 | |
73°F | 2.38 | -- | ft·lb/in2 | |
簡支梁缺口沖擊強度 (73°F) | 25 | -- | ft·lb/in2 | ISO 179 |
懸壁梁缺口沖擊強度 | ||||
73°F | 1.0 | -- | ft·lb/in | ASTM D256 |
-40°F | 1.9 | -- | ft·lb/in2 | ISO 180 |
73°F | 2.9 | -- | ft·lb/in2 | ISO 180 |
Drop Impact Resistance (73°F) | 1.50 | -- | ft·lb | Internal Method |
熱性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
熱變形溫度 | ||||
66 psi | 419 | -- | °F | ISO 75-2 2 |
264 psi, 未退火 | 396 | -- | °F | ASTM D648 |
264 psi | 392 | -- | °F | ISO 75-2 2 |
熔融峰值溫度 | 428 | -- | °F | ASTM D3418, ISO 3146 |
線形膨脹系數 | ||||
流動 | 0.000017 | -- | in/in/°F | ASTM E831, ISO 11359-2 |
橫向 | 0.000037 | -- | in/in/°F | ISO 11359-2 |
RTI Elec (0.0591 in) | 221 | -- | °F | UL 746 |
RTI Imp (0.0591 in) | 221 | -- | °F | UL 746 |
RTI Str (0.0591 in) | 221 | -- | °F | UL 746 |
電氣性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
體積電阻率 | ||||
0.0591 in | > 1.0E+13 | -- | ohm·cm | ASTM D257 |
-- | > 3.9E+12 | -- | ohm·in | IEC 60093 2 |
可燃性 | 干燥 | 調節后的 | 單位制 | 測試方法 |
UL 阻燃等級 (0.0591 in) | HB | -- | UL 94 |
注射 | 干燥 | 單位制 | |
干燥溫度 | 176 | °F | |
干燥時間 | 2.0 到 4.0 | hr | |
建議的zui大水分含量 | 0.10 | % | |
加工(熔體)溫度 | 518 到 563 | °F | |
模具溫度 | 176 到 203 | °F | |
注塑溫度 | 508 到 1810 | psi | |
注射速度 | 快速 |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA6德國巴斯夫 8267G HS BK-102高強度 抗彎曲其它產品
PA6德國巴斯夫 8267G HS BK-102高強度 抗彎曲
PA6德國巴斯夫 8267G HS BK-106抗彎曲 抗紫外線性能良好
PA6德國巴斯夫 8267G HS BK-106A
PA6德國巴斯夫 8267GHS
PA6德國巴斯夫 8253HS BK102 管道 緊固件
PA6德國巴斯夫 8233GH6
PA6德國巴斯夫 8233G HS BK-102良好的抗熱老化性 良好的抗蠕
PA6德國巴斯夫 8233G HS BK-106良好的表面光潔度 良好的抗
PA6德國巴斯夫 8233G HS耐化學性良好 耐磨蝕性,良好 熱穩定性
PA6德國巴斯夫 8233G耐化學性良好 耐磨蝕性,良好 熱穩定性