特性備注:易流動,易脫模,快速固化 重要參數: 成型收縮率:1.14 % 缺口沖擊強度:10 氧指數:26 % 拉伸強度:50 MPa 斷裂伸長率:35 % 彎曲強度:110 MPa 彎曲模量:2900 MPa
產品說明 | ||||
Ultramid 8351 HS BK-102 is a heat stabilized, pigmented black, impact modified type 6 nylon graft copolymer developed for injection molding applications requiring a high level of toughness combined with a moderate flexibility and faster cycles. Excellent thermal and chemical resistance properties provided by the nylon backbone. It demonstrates the highest impact performance within the Ultramid copolymer product line while maintaining an excellent balance of strength and stiffness. Excellent chemical resistance to greases, oils and hydrocarbons. Ultramid 8351 HS BK-102 is generally recommended for applications suchas spray gun and power tool handles, trim clips and fasteners, wall anchors and automotive roof clips rack components. | ||||
總體 | ||||
材料狀態 |
| |||
資料 1 |
| |||
UL 黃卡 2 |
| |||
搜索 UL 黃卡 |
| |||
供貨地區 |
| |||
添加劑 |
| |||
性能特點 |
| |||
用途 |
| |||
RoHS 合規性 |
| |||
外觀 |
| |||
加工方法 |
|
物理性能 | 額定值 | 單位制 | 測試方法 |
比重 | |||
-- | 1.07 | ASTM D792 | |
-- | 1.07 | g/cm3 | ISO 1183 |
收縮率 - 流動 (0.125 in) | 0.014 | in/in | No Standard |
吸水率 | |||
24 hr | 1.1 | % | ASTM D570 |
73°F, 24 hr | 1.1 | % | ISO 62 |
飽和 | 6.7 | % | ASTM D570 |
飽和, 73°F | 6.7 | % | ISO 62 |
平衡, 50% RH | 1.9 | % | ASTM D570 |
平衡, 73°F, 50% RH | 1.9 | % | ISO 62 |
硬度 | 額定值 | 單位制 | 測試方法 |
洛氏硬度 (R 計秤) | 78 | ASTM D785 |
機械性能 | 額定值 | 單位制 | 測試方法 |
拉伸模量 (73°F) | 261000 | psi | ISO 527-2 |
抗張強度 | |||
屈服, 73°F | 7980 | psi | ASTM D638 |
屈服, 73°F | 7110 | psi | ISO 527-2 |
伸長率 | |||
屈服, 73°F | 5.0 | % | ASTM D638, ISO 527-2 |
斷裂, 73°F | > 100 | % | ASTM D638 |
斷張率 (73°F) | > 50 | % | ISO 527-2 |
彎曲模量 | |||
73°F | 245000 | psi | ASTM D790 |
73°F | 218000 | psi | ISO 178 |
彎曲強度 | |||
73°F | 9570 | psi | ASTM D790 |
73°F | 7690 | psi | ISO 178 |
沖擊性能 | 額定值 | 單位制 | 測試方法 |
簡支梁缺口沖擊強度 (73°F) | 44 | ft·lb/in2 | ISO 179 |
簡支梁缺口沖擊強度 (73°F) | 無斷裂 | ISO 179 | |
懸壁梁缺口沖擊強度 | |||
73°F | 無斷裂 | ASTM D256, ISO 180 | |
-40°F | 8.6 | ft·lb/in2 | ISO 180 |
Drop Impact Resistance (73°F) | 210 | ft·lb | Internal Method |
熱性能 | 額定值 | 單位制 | 測試方法 |
熱變形溫度 | |||
264 psi, 未退火 | 131 | °F | ASTM D648 |
264 psi, 未退火 | 120 | °F | ISO 75-2/A |
熔融峰值溫度 | 428 | °F | ASTM D3418, ISO 3146 |
線形膨脹系數 - 流動 | 0.000059 | in/in/°F | ASTM E831 |
RTI Elec (0.0591 in) | 221 | °F | UL 746 |
RTI Imp (0.0591 in) | 221 | °F | UL 746 |
RTI Str (0.0591 in) | 221 | °F | UL 746 |
電氣性能 | 額定值 | 單位制 | 測試方法 |
體積電阻率 | |||
0.0591 in | > 1.0E+15 | ohm·cm | ASTM D257 |
-- | > 1.0E+15 | ohm·cm | IEC 60093 |
可燃性 | 額定值 | 單位制 | 測試方法 |
UL 阻燃等級 (0.0591 in) | HB | UL 94 |
注射 | 額定值 | 單位制 | |
干燥溫度 | 176 | °F | |
干燥時間 | 2.0 到 4.0 | hr | |
建議的zui大水分含量 | 0.20 | % | |
加工(熔體)溫度 | 464 到 518 | °F | |
模具溫度 | 176 到 203 | °F | |
注塑溫度 | 508 到 1810 | psi | |
注射速度 | 快速 |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA6德國巴斯夫 8351HS BK102耐熱性,高 耐碳氫化合物 耐油性能其它產品
PA6德國巴斯夫 8351HS BK102耐熱性,高 耐碳氫化合物 耐油性能
PA6德國巴斯夫 8267G HS BK-102高強度 抗彎曲
PA6德國巴斯夫 8267G HS BK-106抗彎曲 抗紫外線性能良好
PA6德國巴斯夫 8267G HS BK-106A
PA6德國巴斯夫 8267GHS
PA6德國巴斯夫 8253HS BK102 管道 緊固件
PA6德國巴斯夫 8233GH6
PA6德國巴斯夫 8233G HS BK-102良好的抗熱老化性 良好的抗蠕
PA6德國巴斯夫 8233G HS BK-106良好的表面光潔度 良好的抗
PA6德國巴斯夫 8233G HS耐化學性良好 耐磨蝕性,良好 熱穩定性