Vydyne® R220 is a 40% mineral reinforced Nylon 66 resin formulated for improved impact strength. Also available in black as R228. It is an injection molding grade formulated to retain the inherent processing advantages of unreinforced Nylon 66 while enhancing rigidity, strength, and heat resistance. Vydyne R220/R228 maintains the chemical resistance typical of nylon to a wide variety of chemicals, gasoline, oils, greases, and solvents. Vydyne R220/R228 resins utilize a unique mineral reinforced nylon system developed by Ascend Performance Materials to satisfy the market need for a high-rigidity thermoplastic as an alternative to certain metals. This mineral system provides two key features: (1) isotropic behavior — property development in molded parts is usually independent of flow direction. (2) a reduction in the tendency to develop sink marks in heavy cross sections such as molded-in bosses and ribs. While not sink free, parts made from Vydyne R220/R228 can often permit boss and rib design or wall cross section changes that would not be tolerable in other unreinforced thermoplastic materials. Thus Vydyne R220/R228 resins offer more uniform molded part strength and performance as well as wider latitude in part design. Vydyne R220/R228 resins are the workhorses for Ascend Performance Materials full line of mineral reinforced nylon resins, providing the best overall balance of properties. Vydyne R220/R228 are heat stabilized and designed to provide increased ductility and reduced melt viscosity vs. unreinforced materials.This ductility improvement results in tougher, more impact resistant molded parts. The reduction in melt viscosity enhances overall ease of injection molding, resulting in minor reductions in tensile strength, modulus, and heat distortion temperature. Parts from Vydyne R220/R228 have successfully withstood paint bake oven cycles without significant loss of either dimensional stability or part properties. | |
總體 | |
材料狀態 | 已商用:當前有效 |
資料 1 | Processing (English) |
搜索 UL 黃卡 | Ascend Performance Materials LLC.Vydyne® |
供貨地區 | 北美洲歐洲亞太地區 |
填料/增強材料 | 礦物填料, 40% 填料按重量 |
添加劑 | 熱穩定劑 |
性能特點 | 剛性,高抗溶解性抗撞擊性,良好良好的強度耐化學性良好耐汽油性耐熱性,高耐油性能耐油脂性能熱穩定性韌性良好延展性 |
用途 | 齒輪動力/其它工具工業領域:汽車的發動機罩下的零件汽車外部零件凸輪型號 |
機構評級 | ASTM D 4066 PA022M40ASTM D 6779 PA022M40FED L-P-410AMIL M-20693B |
UL 檔案號 | E70062 |
外觀 | 自然色 |
形式 | 顆粒料 |
加工方法 | 注射成型 |
多點數據 | Isothermal Stress vs. Strain (ISO 11403-1) |
物理性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
密度 | 1.48 | -- | g/cm3 | ISO 1183 |
收縮率 | ISO 294-4 | |||
橫向流量: 73°F, 0.0787 in | 1.1 | -- | % | |
流量: 73°F, 0.0787 in | 1.0 | -- | % | |
吸水率 | ISO 62 | |||
73°F, 24 hr | 1.1 | -- | % | |
平衡, 73°F, 50% RH | 1.6 | -- | % |
機械性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
拉伸模量 (73°F) | 1.00E+6 | 377000 | psi | ISO 527-2 |
拉伸應力 (屈服, 73°F) | 14900 | 10600 | psi | ISO 527-2 |
拉伸應變 | ISO 527-2 | |||
屈服, 73°F | 1.5 | 16 | % | |
斷裂, 73°F | 6.0 | 30 | % | |
彎曲模量 (73°F) | 885000 | 334000 | psi | ISO 178 |
彎曲強度 (73°F) | 18000 | 7250 | psi | ISO 178 |
泊松比 | 0.35 | -- | ISO 527 | |
沖擊性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
簡支梁缺口沖擊強度 | ISO 179 | |||
-22°F | 3.0 | -- | ft·lb/in2 | |
73°F | 3.5 | -- | ft·lb/in2 | |
簡支梁缺口沖擊強度 | ISO 179 | |||
-22°F | 52 | -- | ft·lb/in2 | |
73°F | 68 | -- | ft·lb/in2 | |
懸壁梁缺口沖擊強度 (73°F) | 4.3 | -- | ft·lb/in2 | ISO 180 |
熱性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
熱變形溫度 | ||||
66 psi, 未退火 | 432 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 244 | -- | °F | ISO 75-2/A |
維卡軟化溫度 | 460 | -- | °F | ISO 306/B |
溶融溫度(DSC) | 496 | -- | °F | ISO 3146 |
線形膨脹系數 | ISO 11359-2 | |||
流動: 73 到 131°F, 0.0787 in | 3.3E-6 | -- | in/in/°F | |
橫向: 73 到 131°F, 0.0787 in | 3.5E-6 | -- | in/in/°F | |
RTI Elec | UL 746 | |||
0.0295 in | 221 | -- | °F | |
0.0591 in | 221 | -- | °F | |
0.118 in | 221 | -- | °F | |
RTI Imp | UL 746 | |||
0.0295 in | 194 | -- | °F | |
0.0591 in | 194 | -- | °F | |
0.118 in | 194 | -- | °F | |
RTI Str | UL 746 | |||
0.0295 in | 221 | -- | °F | |
0.0591 in | 221 | -- | °F | |
0.118 in | 221 | -- | °F |
電氣性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
體積電阻率 (0.118 in) | 5.5E+16 | -- | ohm·cm | IEC 60093 |
耐電強度 2 (73°F, 0.118 in) | 380 | -- | V/mil | IEC 60243-1 |
耐電弧性 (0.118 in) | PLC 6 | -- | ASTM D495 | |
相比耐漏電起痕指數(CTI) (0.118 in) | PLC 0 | -- | UL 746 | |
漏電起痕指數 (0.118 in) | > 600 | -- | V | IEC 60112 |
高電弧燃燒指數(HAI) | UL 746 | |||
0.0295 in | PLC 0 | -- | ||
0.0591 in | PLC 0 | -- | ||
0.118 in | PLC 0 | -- | ||
高電壓電弧起痕速率 (HVTR) (0.118 in) | PLC 1 | -- | UL 746 | |
熱絲引燃 (HWI) | UL 746 | |||
0.0295 in | PLC 4 | -- | ||
0.0591 in | PLC 4 | -- | ||
0.118 in | PLC 3 | -- | ||
可燃性 | 干燥 | 調節后的 | 單位制 | 測試方法 |
UL 阻燃等級 | UL 94 | |||
0.0295 in, All colors | HB | -- | ||
0.0591 in, All colors | HB | -- | ||
0.118 in, All colors | HB | -- |
注射 | 干燥 | 單位制 | |
干燥溫度 | < 158 | °F | |
干燥時間 | 1.0 到 3.0 | hr | |
建議注入量 | 40 到 80 | % | |
建議的zui大回制料比例 | 25 | % | |
螺筒后部溫度 | 536 到 590 | °F | |
螺筒中部溫度 | 536 到 590 | °F | |
螺筒前部溫度 | 536 到 590 | °F | |
射嘴溫度 | 536 到 590 | °F | |
加工(熔體)溫度 | 545 到 581 | °F | |
模具溫度 | 149 到 203 | °F | |
注塑溫度 | 7980 到 20300 | psi | |
注射速度 | 快速 | ||
保壓 | 7980 到 20300 | psi | |
背壓 | 29.0 到 145 | psi | |
螺桿轉速 | 40 到 120 | rpm | |
合模力 | 1.9 到 4.5 | tons/in2 | |
墊層 | 0.118 到 0.252 | in | |
注射說明 | |||
Injection Time: <1 to 2.5 sec |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA66美國首諾 R-220齒輪 動力/其它工具其它產品
PA66美國首諾 R-220齒輪 動力/其它工具
PA66美國首諾 R-220剛性,汽車外部零件 凸輪
PA66美國首諾 R-220剛性,高 抗溶解性 抗撞擊性,良好 良好的強
PA66美國首諾 R-220熱穩定性 韌性良好 延展性
PA66美國首諾 R-220耐化學性良好 耐汽油性 耐熱性,高 耐油性能
PA66美國首諾 R350-GF25 玻璃纖維增強材料, 25%
PA66美國首諾 J350-GK30 玻璃珠, 30% 填料按重量
PA66美國首諾 J350-GK30
PA66美國首諾 J350-GF50 玻璃纖維增強材料, 50%
PA66美國首諾 J350-GF30 玻璃纖維增強材料, 30%