優勢說明:PA66吸水量:每1%吸水量體積增加0.003in,在50%的相對濕度,23℃的氣溫吸水量是2.5%。收縮率為2.25%,比重1.14G/CM3詳細說明:
1.PA66吸水量:每1%吸水量體積增加0.003in,在50%的相對濕度,23℃的氣溫吸水量是2.5%。收縮率為2.25%,比重1.14G/CM3
: 本公司可以免費提供各種材料認
證
產品說明 | |
The Vydyne R533® Series of 33% glass fiber reinforced nylons are available in natural, black and heat stabilized versions. They are general purpose, injection molding grades which are lubricated for good machine feed, flow and mold release. Vydyne R533 Series resins are members of a wide range of glass reinforced resins supplied by Ascend Performance Materials. Other glass fiber loadings available include 13% and 43%. Vydyne R533 Series resins have tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption, and part weight are key advantages of Vydyne glass reinforced Nylon 6,6 resins over aluminum and/or zinc die cast parts. Vydyne R533H is a heat stabilized grade, formulated to minimize the oxidative and thermal degradation of the nylon polymer when exposed to elevated temperatures for extended periods of time. Vydyne R533H provides improved retention of physical properties under exposure to long-term heat. The continuous operating use temperature is 275°F and short-term peak temperatures as high as 475°F. | |
總體 | |
材料狀態 | 已商用:當前有效 |
資料 1 | Processing (English)Technical Datasheet (English) |
搜索 UL 黃卡 | Ascend Performance Materials LLC.Vydyne® |
供貨地區 | 北美洲歐洲亞太地區 |
填料/增強材料 | 玻璃纖維增強材料, 33% 填料按重量 |
添加劑 | 熱穩定劑潤滑劑 |
性能特點 | 剛性,高高強度經潤滑良好的流動性熱穩定性脫模性能良好 |
用途 | 齒輪動力/其它工具汽車的發動機罩下的零件型號 |
機構評級 | ASTM D 4066 PA012G35ASTM D 6779 PA012G35FED L-P-410AMIL M-20693B |
UL 檔案號 | E70062 |
外觀 | 黑色自然色 |
形式 | 顆粒料 |
加工方法 | 注射成型 |
多點數據 | Isothermal Stress vs. Strain (ISO 11403-1)Tensile Stress vs. Strain (ASTM D638) |
物理性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
密度 | 1.40 | -- | g/cm3 | ISO 1183 |
收縮率 | ISO 294-4 | |||
橫向流量: 73°F, 0.0787 in | 0.90 | -- | % | |
流量: 73°F, 0.0787 in | 0.40 | -- | % | |
吸水率 | ISO 62 | |||
73°F, 24 hr | 0.80 | -- | % | |
平衡, 73°F, 50% RH | 1.8 | -- | % |
機械性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
拉伸模量 (73°F) | 1.48E+6 | 1.15E+6 | psi | ISO 527-2 |
拉伸應力 (斷裂, 73°F) | 29700 | 21500 | psi | ISO 527-2 |
拉伸應變 (斷裂, 73°F) | 3.0 | 5.0 | % | ISO 527-2 |
彎曲模量 (73°F) | 1.41E+6 | 943000 | psi | ISO 178 |
彎曲強度 (73°F) | 42000 | 29700 | psi | ISO 178 |
泊松比 | 0.40 | -- | ISO 527-2 | |
沖擊性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
簡支梁缺口沖擊強度 | ISO 179 | |||
-22°F | 5.6 | -- | ft·lb/in2 | |
73°F | 5.9 | -- | ft·lb/in2 | |
簡支梁缺口沖擊強度 | ISO 179 | |||
-22°F | 36 | -- | ft·lb/in2 | |
73°F | 40 | -- | ft·lb/in2 | |
懸壁梁缺口沖擊強度 (73°F) | 5.6 | -- | ft·lb/in2 | ISO 180 |
熱性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
熱變形溫度 | ||||
66 psi, 未退火 | 500 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 482 | -- | °F | ISO 75-2/A |
維卡軟化溫度 | 486 | -- | °F | ISO 306/B |
溶融溫度(DSC) | 500 | -- | °F | ISO 3146 |
線形膨脹系數 | ISO 11359-2 | |||
流動: 73 到 131°F, 0.0787 in | 1.1E-6 | -- | in/in/°F | |
橫向: 73 到 131°F, 0.0787 in | 5.0E-6 | -- | in/in/°F | |
RTI Elec | UL 746 | |||
0.0295 in | 284 | -- | °F | |
0.0591 in | 284 | -- | °F | |
0.118 in | 284 | -- | °F | |
RTI Imp | UL 746 | |||
0.0295 in | 257 | -- | °F | |
0.0591 in | 257 | -- | °F | |
0.118 in | 257 | -- | °F | |
RTI Str | UL 746 | |||
0.0295 in | 284 | -- | °F | |
0.0591 in | 284 | -- | °F | |
0.118 in | 284 | -- | °F |
電氣性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
體積電阻率 (0.118 in) | 3.0E+15 | -- | ohm·cm | IEC 60093 |
耐電強度 2 (73°F, 0.118 in) | 410 | -- | V/mil | IEC 60243-1 |
耐電弧性 (0.118 in) | PLC 6 | -- | ASTM D495 | |
相比耐漏電起痕指數(CTI) (0.118 in) | PLC 2 | -- | UL 746 | |
漏電起痕指數 (0.118 in) | 400 到 599 | -- | V | IEC 60112 |
高電弧燃燒指數(HAI) | UL 746 | |||
0.0295 in | PLC 0 | -- | ||
0.0591 in | PLC 0 | -- | ||
0.118 in | PLC 0 | -- | ||
高電壓電弧起痕速率 (HVTR) (0.118 in) | PLC 1 | -- | UL 746 | |
熱絲引燃 (HWI) | UL 746 | |||
0.0295 in | PLC 4 | -- | ||
0.0591 in | PLC 3 | -- | ||
0.118 in | PLC 4 | -- | ||
可燃性 | 干燥 | 調節后的 | 單位制 | 測試方法 |
UL 阻燃等級 | UL 94 | |||
0.0295 in, All colors | HB | -- | ||
0.0591 in, All colors | HB | -- | ||
0.118 in, All colors | HB | -- | ||
極限氧指數 | 28 | -- | % | ASTM D2863 |
注射 | 干燥 | 單位制 | |
干燥溫度 | < 158 | °F | |
干燥時間 | 1.0 到 3.0 | hr | |
建議注入量 | 40 到 80 | % | |
建議的zui大回制料比例 | 25 | % | |
螺筒后部溫度 | 536 到 590 | °F | |
螺筒中部溫度 | 536 到 590 | °F | |
螺筒前部溫度 | 536 到 590 | °F | |
射嘴溫度 | 536 到 590 | °F | |
加工(熔體)溫度 | 545 到 581 | °F | |
模具溫度 | 149 到 203 | °F | |
注塑溫度 | 7980 到 20300 | psi | |
注射速度 | 快速 | ||
保壓 | 7980 到 20300 | psi | |
背壓 | 29.0 到 145 | psi | |
螺桿轉速 | 60 到 120 | rpm | |
合模力 | 1.9 到 4.5 | tons/in2 | |
墊層 | 0.118 到 0.252 | in | |
注射說明 | |||
Injection Time: <1 to 2.5 sec |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA66美國首諾 R533H經潤滑 良好的流動性其它產品
PA66美國首諾 R533H經潤滑 良好的流動性
PA66美國首諾 R533 T玻璃纖維增強材料, 33% 潤滑劑
PA66美國首諾 R533H BAT玻璃纖維增強材料, 33% 潤滑劑
PA66美國首諾 R513H良好的流動性 耐化學性良好 耐汽油性
PA66美國首諾 R513H BK良好的流動性 耐化學性良好 耐汽油性
PA66美國首諾 R513H BK玻璃纖維增強材料, 13% 填料按重量
PA66美國首諾 R-220 礦物填料, 40% 填料按重量
PA66美國首諾 R-220齒輪 動力/其它工具
PA66美國首諾 R-220剛性,汽車外部零件 凸輪
PA66美國首諾 R-220剛性,高 抗溶解性 抗撞擊性,良好 良好的強