優勢說明:PA66吸水量:每1%吸水量體積增加0.003in,在50%的相對濕度,23℃的氣溫吸水量是2.5%。收縮率為2.25%,比重1.14G/CM3詳細說明:
1.PA66吸水量:每1%吸水量體積增加0.003in,在50%的相對濕度,23℃的氣溫吸水量是2.5%。收縮率為2.25%,比重1.14G/CM3
: 本公司可以免費提供各種材料認
證
產品說明 | |
Material code according to ISO 1043-1: PA66 Nylon 66 reinforced by 40 weight percent long glass fibers. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Can be used for substituting die cast metal with the advantage of Weight reduction, no corrosion problems, no post treatment. | |
總體 | |
材料狀態 | 已商用:當前有效 |
資料 1 | Technical Datasheet - ISO (English) |
搜索 UL 黃卡 | TiconaCelstran® |
供貨地區 | 歐洲 |
填料/增強材料 | 長玻璃纖維, 40% 填料按重量 |
性能特點 | 低翹曲性剛性,高高強度抗撞擊性,良好良好的抗蠕變性耐低溫撞擊耐熱性,高 |
用途 | 金屬置換 |
RoHS 合規性 | 制造商 |
形式 | 顆粒料 |
加工方法 | 注射成型 |
樹脂ID (ISO 1043) | PA66 |
機械性能 | 額定值 | 單位制 | 測試方法 |
拉伸模量 (176°F) | 1.13E+6 | psi | ISO 527-2/1A |
拉伸應力 (176°F) | 19600 | psi | ISO 527-2/1A |
拉伸應變 (斷裂, 176°F) | 2.5 | % | ISO 527-2/1A |
彎曲模量 | ISO 178 | ||
73°F | 1.61E+6 | psi | |
176°F | 1.04E+6 | psi | |
彎曲強度 | ISO 178 | ||
73°F | 43500 | psi | |
176°F | 31200 | psi | |
沖擊性能 | 額定值 | 單位制 | 測試方法 |
簡支梁缺口沖擊強度 | ISO 179/1eA | ||
-22°F | 17 | ft·lb/in2 | |
73°F | 17 | ft·lb/in2 | |
懸壁梁缺口沖擊強度 | ISO 180/1A | ||
-22°F | 30 | ft·lb/in2 | |
73°F | 31 | ft·lb/in2 |
注射 | 額定值 | 單位制 | |
干燥溫度 | 158 到 176 | °F | |
干燥時間 | 2.0 到 4.0 | hr | |
建議的zui大水分含量 | 0.15 | % | |
料筒溫度 | 158 到 176 | °F | |
螺筒后部溫度 | 509 到 527 | °F | |
螺筒中部溫度 | 527 到 545 | °F | |
螺筒前部溫度 | 545 到 563 | °F | |
射嘴溫度 | 581 到 599 | °F | |
加工(熔體)溫度 | 581 到 599 | °F | |
模具溫度 | 194 到 248 | °F | |
注塑溫度 | 17400 到 21800 | psi | |
注射速度 | 中等 | ||
保壓 | 7250 到 11600 | psi | |
背壓 | 0.00 到 435 | psi | |
注射說明 | |||
Manifold Temperature: 300 to 315°C Zone 4 Temperature: 295 to 305°C Feed Temperature: 20 to 50°C |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA66美國泰科納 GF40-01抗撞擊性,良好 良好的抗蠕變性 耐低溫撞擊其它產品
PA66美國泰科納 GF40-01抗撞擊性,良好 良好的抗蠕變性 耐低溫撞擊
PA66美國泰科納 7523-2AM 耐水解性熱穩定性
PA66美國泰科納 7020-2 NF20017耐水解性 熱穩定性
PA66美國泰科納 1503-2F BK ND3007耐水解性 熱穩定性
PA66美國泰科納1503-2 BK ND3007尺寸穩定性良好熱穩定性
PA66美國泰科納1503-2 BK尺寸穩定性良好熱穩定性
PA66美國首諾 R533H BK熱穩定性 脫模性能良好
PA66美國首諾 R533T高拉伸強度 耐化學性良好 熱穩定性
PA66美國首諾 R533H經潤滑 良好的流動性
PA66美國首諾 R533 T玻璃纖維增強材料, 33% 潤滑劑