品名:聚酰胺6或尼龍6(PA6)分子式:[-NH-(CH2)5-CO]n-性狀:半透明或不透明乳白色結晶形聚合物特性:熱塑性、輕質、韌性好、耐化學品和耐久性好燃燒鑒別方法:藍底黃火焰,燒植物味溶劑實驗:耐環己酮和芳香溶劑密度:1.13g/cm3熔點:215℃熱分解溫度:>300℃平衡吸水率:3.5%具有良好的耐磨性、自潤滑性和耐溶劑性。密 度:(g/cm3) 1.14-1.15熔 點:215-225℃拉伸強度:> 60.0Mpa伸 長 率:> 30%彎曲強度: 90.0Mpa缺口沖擊強度:(KJ/m2) > 5本公司 可以免費提供各種材料物性及各種材質認證 如:SGS UL MSDS ROHS MDS 等證明 :
LNP™ COLORCOMP™ PX99848 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ FARADEX™ PS003E compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ FARADEX™ PS003E compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ FARADEX™ PS003E compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PTF2BXXX compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ KONDUIT™ PTF2BXXX compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PTF2BXXX compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PX08321 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PX08321 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ KONDUIT™ PX08321 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PX08322 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PX08322 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ KONDUIT™ PX08322 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PX09322 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PX10322 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PX11311 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PX11311 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PX11311U compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PX11313 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ KONDUIT™ PX11313 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ KONDUIT™ PX11422 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ PFI12R compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ PFI12R compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ LUBRICOMP™ PFL36 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ PFL36 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ LUBRICOMP™ PFL38S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ PFN16 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ PFN16 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ LUBRICOMP™ PFP36 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ PFP36 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ LUBRICOMP™ PI001 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ LUBRICOMP™ PL002 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ RFN16 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ LUBRICOMP™ RFN16 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ STAT-KON™ PD000 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-KON™ PE002Z compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ STAT-KON™ PFD04 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ STAT-KON™ PFD04ES compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-KON™ PFD04S compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-KON™ PFD06 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ STAT-KON™ PFD06 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ STAT-KON™ PX05047 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-KON™ PX08024 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-KON™ PX93058 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-LOY™ P3000U compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ STAT-LOY™ PF303 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ STAT-LOY™ PF303 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ STAT-LOY™ PF306 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PB006EQ compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PB006SXS compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PC006 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF001S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF001S compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF002 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF003 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF003 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF004 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF004S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF004S compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF005 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF005S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF005S compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF006 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF006S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF006S compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF006U compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF006U compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF006U compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF007 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF008 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF008 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF008QS compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF008S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF008S compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF009 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF009 compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF00A compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF00A compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF00ASXS compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF00ASXS compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF00C compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PF00C compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PF00C compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF00CS compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PF1006HI005 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PFB55 compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PFB91S compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PFW53U compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PFW53U compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PFW64 compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PH0220AC compound | SABIC Innovative Plastics Europe | 尼龍6 | |
LNP™ THERMOCOMP™ PH0240A compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PH0320A compound | SABIC Innovative Plastics | 尼龍6 | |
LNP™ THERMOCOMP™ PH0320A compound | SABIC Innovative Plastics Asia Pacific | 尼龍6 | |
LNP™ THERMOCOMP™ PH0400CX_BK1D466 compound | SABIC Innovative Plastics | 尼龍6 |
產品說明 | |
LNP THERMOCOMP* PF006 is a compound based on Nylon 6 resin containing 30% Glass Fiber. Also known as: LNP* Thermocomp* Compound PF-1006 Product reorder name: PF006 | |
總體 | |
材料狀態 |
|
資料 1 |
|
UL 黃卡 2 |
|
搜索 UL 黃卡 |
|
供貨地區 |
|
填料/增強材料 |
|
加工方法 |
|
物理性能 | 額定值 | 單位制 | 測試方法 |
密度 | 1.37 | g/cm3 | ISO 1183, ASTM D792 |
收縮率 | |||
流動: 24小時 | 0.20 到 0.50 | % | ASTM D955 |
橫向流動: 24小時 | 1.0 到 1.2 | % | ASTM D955 |
橫向流量: 24小時 | 1.0 到 1.2 | % | ISO 294-4 |
流量: 24小時 | 0.17 到 0.50 | % | ISO 294-4 |
吸水率 | |||
24 hr, 50% RH | 0.86 | % | ASTM D570 |
平衡, 23°C, 50% RH | 1.5 | % | ISO 62 |
機械性能 | 額定值 | 單位制 | 測試方法 |
拉伸模量 | |||
-- 3 | 8760 | MPa | ASTM D638 |
-- | 8580 | MPa | ISO 527-2/1 |
抗張強度 | |||
斷裂 | 130 | MPa | ASTM D638 |
斷裂 | 128 | MPa | ISO 527-2 |
伸長率 | |||
斷裂 | 2.8 | % | ASTM D638 |
斷裂 | 2.9 | % | ISO 527-2 |
彎曲模量 | |||
-- | 6960 | MPa | ASTM D790 |
-- | 7970 | MPa | ISO 178 |
彎曲強度 | |||
-- | 201 | MPa | ASTM D790 |
-- | 204 | MPa | ISO 178 |
沖擊性能 | 額定值 | 單位制 | 測試方法 |
懸壁梁缺口沖擊強度 | |||
23°C | 120 | J/m | ASTM D256 |
23°C 4 | 8.2 | kJ/m2 | ISO 180/1A |
無缺口懸臂梁沖擊 | |||
23°C | 830 | J/m | ASTM D4812 |
23°C 4 | 55 | kJ/m2 | ISO 180/1U |
裝有測量儀表的落鏢沖擊 | |||
23°C, Energy at Peak Load | 9.10 | J | ASTM D3763 |
-- | 2.68 | J | ISO 6603-2 |
熱性能 | 額定值 | 單位制 | 測試方法 |
熱變形溫度 | |||
0.45 MPa, 未退火, 3.20 mm | 219 | °C | ASTM D648 |
1.8 MPa, 未退火, 3.20 mm | 206 | °C | ASTM D648 |
1.8 MPa, 未退火, 64.0 mm 跨距 5 | 203 | °C | ISO 75-2/Af |
線形膨脹系數 | ASTM E831, ISO 11359-2 | ||
流動: -40 到 40°C | 0.000031 | cm/cm/°C | |
橫向: -40 到 40°C | 0.000067 | cm/cm/°C |
可燃性 | 額定值 | 測試方法 | |
UL 阻燃等級 (1.50 mm, Testing by SABIC) | HB | UL 94 |
注射 | 額定值 | 單位制 | |
干燥溫度 | 82.2 | °C | |
干燥時間 | 4.0 | hr | |
建議的zui大水分含量 | 0.15 到 0.25 | % | |
螺筒后部溫度 | 249 到 260 | °C | |
螺筒中部溫度 | 266 到 277 | °C | |
螺筒前部溫度 | 277 到 288 | °C | |
加工(熔體)溫度 | 266 到 277 | °C | |
模具溫度 | 82.2 到 93.3 | °C | |
背壓 | 0.344 到 0.689 | MPa | |
螺桿轉速 | 30 到 60 | rpm |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA6, 美國液氮, PF006 玻璃纖維增強材料, 30%其它產品
PA6, 美國液氮, PF006 玻璃纖維增強材料, 30%
PA6, 美國液氮, PF005S 玻璃纖維增強材料, 25
PA6, 美國液氮, PF005 玻璃纖維增強材料, 25%
PA6, 美國液氮, PF004S 玻璃纖維增強材料, 20%
PA6, 美國液氮, PF004 玻璃纖維增強材料, 20% 填料
PA6, 美國液氮, PF003 玻璃纖維增強材料, 15%
PA6, 美國液氮, PF002 玻璃纖維增強材料, 10% 填
PA6, 美國液氮, PF001S 玻璃纖維增強材料 添加劑
PA6, 美國液氮, PC006 碳纖維增強材料
PA6, 美國液氮, PB006SXS RoHS 合規