品名:聚酰胺6或尼龍6(PA6)分子式:[-NH-(CH2)5-CO]n-性狀:半透明或不透明乳白色結晶形聚合物特性:熱塑性、輕質、韌性好、耐化學品和耐久性好燃燒鑒別方法:藍底黃火焰,燒植物味溶劑實驗:耐環己酮和芳香溶劑密度:1.13g/cm3熔點:215℃熱分解溫度:>300℃平衡吸水率:3.5%具有良好的耐磨性、自潤滑性和耐溶劑性。密 度:(g/cm3) 1.14-1.15熔 點:215-225℃拉伸強度:> 60.0Mpa伸 長 率:> 30%彎曲強度: 90.0Mpa缺口沖擊強度:(KJ/m2) > 5本公司 可以免費提供各種材料物性及各種材質認證 如:SGS UL MSDS ROHS MDS 等證明 :
SCHULAMID® 6 GB 15 LS | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GB 30 LS | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GB 30 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GBF 3010 H | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GBF 3015 FR 4 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GBF 3026 H BLACK 96.8069 LW | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 FR 4 K1681 BLACK 96.8076 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 FR 4 K1681 DEEP BLACK 96.8086 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 FR 4 K1681 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 HI BM | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 HI K2073 SCHWARZ 96.8001 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 HI | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 HV | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 20 H LS | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 25 FR 2 A | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 25 FR | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 25 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 FR 2 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 FR 4 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 FR2 A LM WEISS 96.0342 LM | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 GID LS | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 GID | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 H BLACK REC | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 H LW | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 H | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 HI K1871 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 HI WIT | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 HI | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 TC | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 35 H BLACK REC | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 35 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 40 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 50 TSU | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 50 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 HV 0 H FR | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 HV 11 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 HV 2 FR | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MBF 6010 H | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MGF 45 FR 6 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MKF 3010 H | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MKF 3010 HI | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MKF 4015 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MT 25 FR | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MT 30 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV 13 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV 14 FR 4 K1681 BLACK 96.8076 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV 14 FR 4 K1681 DEEP BLACK 96.8086 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV 14 FR 4 K1681 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV 14 FR | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV 14 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV HI K1893 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV HI | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV SHI | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 NV 12 FR | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 NV 12 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 NV SI | A. Schulman Europe | 尼龍6 | |
SCHULAMID® B 6 MKF 4015 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® B 6 MV | A. Schulman Europe | 尼龍6 | |
SCHULAMID® T MV | A. Schulman Europe | 尼龍6 | |
SCHULATEC® TinCo 50 | A. Schulman Europe | 尼龍 |
產品說明 | ||||
30% glass bead reinforced Polyamide 6 with higher stiffness and dimension stability | ||||
總體 | ||||
材料狀態 |
| |||
資料 1 |
| |||
UL 黃卡 2 |
| |||
搜索 UL 黃卡 |
| |||
供貨地區 |
| |||
填料/增強材料 |
| |||
性能特點 |
| |||
UL 檔案號 |
| |||
加工方法 |
| |||
樹脂ID (ISO 1043) |
|
物理性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
密度 | 1.36 | -- | g/cm3 | ISO 1183/A |
吸水率 (平衡, 23°C, 50% RH) | 2.2 | -- | % | ISO 62 |
粘數 | 145 | -- | cm3/g | ISO 307 |
硬度 | 干燥 | 調節后的 | 單位制 | 測試方法 |
球壓硬度 (H 358/30) | 165 | 105 | MPa | ISO 2039-1 |
機械性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
拉伸模量 | 4000 | 1200 | MPa | ISO 527-2/1A/1 |
拉伸應力 (斷裂) | 70.0 | 34.0 | MPa | ISO 527-2/1A/5 |
拉伸應變 (斷裂) | 10 | 50 | % | ISO 527-2/1A/5 |
彎曲模量 | 3000 | -- | MPa | ISO 178 |
彎曲強度 | 100 | -- | MPa | ISO 178 |
Flexural Strain at Flexural Strength | 6.5 | -- | % | ISO 178 |
沖擊性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
簡支梁缺口沖擊強度 | ISO 179/1eA | |||
-30°C | 3.0 | -- | kJ/m2 | |
23°C | 5.0 | 14 | kJ/m2 | |
簡支梁缺口沖擊強度 | ISO 179/1eU | |||
-30°C | 28 | -- | kJ/m2 | |
23°C | 35 kJ/m2 | 無斷裂 |
熱性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
熱變形溫度 | ||||
0.45 MPa, 未退火 | 180 | -- | °C | ISO 75-2/Bf |
1.8 MPa, 未退火 | 68.0 | -- | °C | ISO 75-2/Af |
維卡軟化溫度 | ||||
-- | 215 | -- | °C | ISO 306/A50 |
-- | 200 | -- | °C | ISO 306/B50 |
Ball Pressure Test (105°C) | Pass | -- | IEC 60695-10-2 |
電氣性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
表面電阻率 | > 1.0E+15 | > 1.0E+12 | ohm | IEC 60093 |
體積電阻率 | > 1.0E+13 | > 1.0E+10 | ohm·cm | IEC 60093 |
漏電起痕指數 | 450 | -- | V | IEC 60112 |
可燃性 | 干燥 | 調節后的 | 單位制 | 測試方法 |
燃燒速率 | < 100 | -- | mm/min | ISO 3795 |
可燃性等級 | IEC 60695-11-10, -20 | |||
1.50 mm | HB | -- | ||
3.00 mm | HB | -- | ||
灼熱絲易燃指數 | IEC 60695-2-12 | |||
1.50 mm | -- | 650 | °C | |
3.00 mm | -- | 650 | °C |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA6 , 美國舒爾曼 , 6 GB 30 低翹曲性 良好的表面光潔度 耐其它產品
PA6 , 美國舒爾曼 , 6 GB 30 低翹曲性 良好的表面光潔度 耐
PA6 , 美國舒爾曼 , 6 GB 30 LS
PA6 , 美國舒爾曼 , 6 GB 15 LS 玻璃珠, 15%
PA6 ,美國舒爾曼 , 6 GF 15 玻璃纖維增強材料, 15%
PA6 / 美國杜邦 / ST811HS NC010 良好的耐熱老化性能
PA6 / 美國杜邦 / ST811HS BK038 襯里 電纜護套
PA6 / 美國杜邦 / ST7301 NC010 超高韌性 改良抗撞擊
PA6 / 美國杜邦 / ST7301 BK356 耐油性能 耐油脂性能
PA6 / 美國杜邦 / PLUS PLS93G35DH1 BK261 汽車
PA6 / 美國杜邦 / FN727 NC010A 良好的柔韌性 耐化