品名:聚酰胺6或尼龍6(PA6)分子式:[-NH-(CH2)5-CO]n-性狀:半透明或不透明乳白色結(jié)晶形聚合物特性:熱塑性、輕質(zhì)、韌性好、耐化學(xué)品和耐久性好燃燒鑒別方法:藍底黃火焰,燒植物味溶劑實驗:耐環(huán)己酮和芳香溶劑密度:1.13g/cm3熔點:215℃熱分解溫度:>300℃平衡吸水率:3.5%具有良好的耐磨性、自潤滑性和耐溶劑性。密 度:(g/cm3) 1.14-1.15熔 點:215-225℃拉伸強度:> 60.0Mpa伸 長 率:> 30%彎曲強度: 90.0Mpa缺口沖擊強度:(KJ/m2) > 5本公司 可以免費提供各種材料物性及各種材質(zhì)認(rèn)證 如:SGS UL MSDS ROHS MDS 等證明 :
SCHULAMID® 6 GB 15 LS | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GB 30 LS | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GB 30 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GBF 3010 H | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GBF 3015 FR 4 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GBF 3026 H BLACK 96.8069 LW | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 FR 4 K1681 BLACK 96.8076 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 FR 4 K1681 DEEP BLACK 96.8086 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 FR 4 K1681 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 HI BM | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 HI K2073 SCHWARZ 96.8001 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 HI | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 HV | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 15 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 20 H LS | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 25 FR 2 A | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 25 FR | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 25 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 FR 2 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 FR 4 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 FR2 A LM WEISS 96.0342 LM | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 GID LS | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 GID | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 H BLACK REC | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 H LW | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 H | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 HI K1871 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 HI WIT | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 HI | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 TC | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 30 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 35 H BLACK REC | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 35 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 40 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 50 TSU | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 GF 50 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 HV 0 H FR | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 HV 11 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 HV 2 FR | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MBF 6010 H | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MGF 45 FR 6 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MKF 3010 H | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MKF 3010 HI | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MKF 4015 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MT 25 FR | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MT 30 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV 13 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV 14 FR 4 K1681 BLACK 96.8076 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV 14 FR 4 K1681 DEEP BLACK 96.8086 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV 14 FR 4 K1681 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV 14 FR | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV 14 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV HI K1893 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV HI | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 MV SHI | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 NV 12 FR | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 NV 12 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® 6 NV SI | A. Schulman Europe | 尼龍6 | |
SCHULAMID® B 6 MKF 4015 | A. Schulman Europe | 尼龍6 | |
SCHULAMID® B 6 MV | A. Schulman Europe | 尼龍6 | |
SCHULAMID® T MV | A. Schulman Europe | 尼龍6 | |
SCHULATEC® TinCo 50 | A. Schulman Europe | 尼龍 |
產(chǎn)品說明 | ||||
30% glass fibre reinforced flame-retardant Polyamide 6 grade; halogen free | ||||
總體 | ||||
材料狀態(tài) |
| |||
資料 1 |
| |||
搜索 UL 黃卡 |
| |||
供貨地區(qū) |
| |||
填料/增強材料 |
| |||
性能特點 |
| |||
加工方法 |
| |||
樹脂ID (ISO 1043) |
|
物理性能 | 額定值 | 單位制 | 測試方法 |
密度 | 1.61 | g/cm3 | ISO 1183/A |
機械性能 | 額定值 | 單位制 | 測試方法 |
拉伸模量 | 12700 | MPa | ISO 527-2/1A/1 |
拉伸應(yīng)力 (斷裂) | 130 | MPa | ISO 527-2/1A/5 |
拉伸應(yīng)變 (斷裂) | 1.5 | % | ISO 527-2/1A/5 |
彎曲模量 | 11900 | MPa | ISO 178 |
彎曲強度 2 (2.0% 應(yīng)變) | 200 | MPa | ISO 178 |
沖擊性能 | 額定值 | 單位制 | 測試方法 |
簡支梁缺口沖擊強度 | ISO 179/1eA | ||
-30°C | 4.0 | kJ/m2 | |
23°C | 5.0 | kJ/m2 | |
簡支梁缺口沖擊強度 | ISO 179/1eU | ||
-30°C | 25 | kJ/m2 | |
23°C | 30 | kJ/m2 |
熱性能 | 額定值 | 單位制 | 測試方法 |
熱變形溫度 | |||
0.45 MPa, 未退火 | 215 | °C | ISO 75-2/Bf |
1.8 MPa, 未退火 | 200 | °C | ISO 75-2/Af |
維卡軟化溫度 | |||
-- | 225 | °C | ISO 306/A50 |
-- | 205 | °C | ISO 306/B50 |
電氣性能 | 額定值 | 單位制 | 測試方法 |
漏電起痕指數(shù) | 375 | V | IEC 60112 |
可燃性 | 額定值 | 單位制 | 測試方法 |
UL 阻燃等級 | UL 94, IEC 60695-11-10, -20 | ||
0.800 mm | V-0 | ||
1.60 mm | V-0 | ||
3.20 mm | V-0 | ||
灼熱絲易燃指數(shù) | IEC 60695-2-12 | ||
0.750 mm | 960 | °C | |
1.50 mm | 960 | °C | |
3.00 mm | 960 | °C | |
熱燈絲點火溫度 | IEC 60695-2-13 | ||
0.750 mm | 750 | °C | |
1.50 mm | 750 | °C | |
3.00 mm | 775 | °C |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA6 , 美國舒爾曼 , 6 GF 30 FR2 A LM WEISS其它產(chǎn)品
PA6 , 美國舒爾曼 , 6 GF 30 GID LS
PA6 , 美國舒爾曼 , 6 GF 30 FR2 A LM WEISS
PA6 , 美國舒爾曼 , 6 GF 30 FR 4 良好的強度 阻燃性
PA6 , 美國舒爾曼 , 6 GF 30 FR 2 無鹵 阻燃性能
PA6 , 美國舒爾曼 , 6 GF 25 剛性,良好 耐油性能 中等粘性
PA6 , 美國舒爾曼 , 6 GF 25 FR 良好的電氣性能 磷含量
PA6 , 美國舒爾曼 , 6 GF 25 FR 2 A
PA6 , 美國舒爾曼 , 6 GF 20 H LS 玻璃纖維增強材料
PA6 , 美國舒爾曼 , 6 GF 15 良好的流動性 耐油性能
PA6 , 美國舒爾曼 , 6 GF 15 HV 耐油性能 韌性良好