Ultramid 8233G HS BK-102 is a heat stabilized, black pigmented,33% glass fiber reinforced PA6 injection molding compound. The higher glass fiber reinforcement results in excellent strength, stiffness, high temperature performance and dimensional stability with a high resistance to creep under load. The heat stabilizer system extends properties at elevated temperatures. It offers easy processing and good aesthetics. It maintains its inherent chemical resistance to greases, oils and hydrocarbons. It is suited for metal replacement. | |
總體 | |
材料狀態(tài) | 已商用:當前有效 |
資料 1 | Processing - Injection Molding (English)Processing - Injection Molding Cooling Times (English)Technical Datasheet - ASTM (English)Technical Datasheet - ISO (English) |
UL 黃卡 2 | E36632-231130 |
搜索 UL 黃卡 | BASF CorporationUltramid® |
供貨地區(qū) | 北美洲 |
填料/增強材料 | 玻璃纖維增強材料, 33% 填料按重量 |
添加劑 | 熱穩(wěn)定劑 |
性能特點 | 半結(jié)晶尺寸穩(wěn)定性良好低粘度剛性,高剛性,良好高強度可加工性,良好良好的表面光潔度良好的抗熱老化性良好的抗蠕變性良好的流動性耐化學性良好耐磨蝕性,良好熱穩(wěn)定性熱穩(wěn)定性,良好 |
用途 | 齒輪電線電纜應(yīng)用動力/其它工具連接器零件裝置汽車的發(fā)動機罩下的零件汽車領(lǐng)域的應(yīng)用: |
機構(gòu)評級 | ULC Unspecified Rating |
RoHS 合規(guī)性 | RoHS 合規(guī) |
外觀 | 黑色 |
形式 | 顆粒料 |
加工方法 | 注射成型 |
物理性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
比重 | ||||
-- | 1.39 | -- | ASTM D792 | |
-- | 0.0502 | -- | lb/in3 | ISO 1183 3 |
收縮率 - 流動 (0.125 in) | 0.0030 | -- | in/in | ASTM D955 |
吸水率 | ||||
24 hr | 1.1 | -- | % | ASTM D570 |
73°F, 24 hr | 1.1 | -- | % | ISO 62 |
飽和 | 6.4 | -- | % | ASTM D570, ISO 62 3 |
平衡, 50% RH | 1.8 | -- | % | ASTM D570 |
平衡 | 1.8 | -- | % | ISO 62 3 |
硬度 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
洛氏硬度 (R 計秤) | 121 | -- | ASTM D785 |
機械性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
拉伸模量 | ||||
-40°F | 1.49E+6 | -- | psi | ISO 527-2 |
176°F | 699000 | -- | psi | ISO 527-2 |
250°F | 582000 | -- | psi | ISO 527-2 |
-- | 1.48E+6 | 812000 | psi | ISO 527-2 3 |
抗張強度 | ||||
斷裂, -40°F | 33400 | -- | psi | ASTM D638, ISO 527-2 |
斷裂, 73°F | 26100 | 14400 | psi | ASTM D638 |
斷裂, 176°F | 13100 | -- | psi | ASTM D638, ISO 527-2 |
斷裂, 250°F | 10200 | -- | psi | ASTM D638, ISO 527-2 |
斷裂 | 24700 | 14400 | psi | ISO 527-2 3 |
伸長率 | ||||
斷裂, 73°F | 3.5 | 7.0 | % | ASTM D638 |
斷裂 | 3.0 | 7.0 | % | ISO 527-2 3 |
彎曲模量 | ||||
73°F | 1.30E+6 | -- | psi | ASTM D790 |
73°F | 1.23E+6 | 754000 | psi | ISO 178 |
彎曲強度 | ||||
73°F | 40600 | -- | psi | ASTM D790 |
73°F | 35500 | 18900 | psi | ISO 178 |
沖擊性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
簡支梁缺口沖擊強度 | ISO 179/1eA 3 | |||
-22°F | 4.76 | -- | ft·lb/in2 | |
73°F | 4.76 | -- | ft·lb/in2 | |
簡支梁缺口沖擊強度 (73°F) | 31 | -- | ft·lb/in2 | ISO 179 |
懸壁梁缺口沖擊強度 (73°F) | 2.1 | -- | ft·lb/in | ASTM D256 |
Drop Impact Resistance (73°F) | 3.00 | -- | ft·lb | Internal Method |
熱性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測試方法 |
熱變形溫度 | ||||
66 psi, 未退火 | 424 | -- | °F | ASTM D648 |
66 psi | 419 | -- | °F | ISO 75-2 3 |
264 psi, 未退火 | 406 | -- | °F | ASTM D648 |
264 psi | 401 | -- | °F | ISO 75-2 3 |
熔融峰值溫度 | 428 | -- | °F | ASTM D3418, ISO 3146 |
線形膨脹系數(shù) - 流動 | 0.000021 | -- | in/in/°F | ASTM E831 |
RTI Elec (0.0591 in) | 284 | -- | °F | UL 746 |
RTI Imp (0.0591 in) | 239 | -- | °F | UL 746 |
RTI Str (0.0591 in) | 284 | -- | °F | UL 746 |
可燃性 | 干燥 | 調(diào)節(jié)后的 | 測試方法 | |
UL 阻燃等級 (0.0591 in) | HB | -- | UL 94 |
注射 | 干燥 | 單位制 | |
干燥溫度 | 176 | °F | |
干燥時間 | 2.0 到 4.0 | hr | |
建議的zui大水分含量 | 0.10 | % | |
加工(熔體)溫度 | 518 到 563 | °F | |
模具溫度 | 176 到 203 | °F | |
注塑溫度 | 508 到 1810 | psi | |
注射速度 | 快速 |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA66美國巴斯夫8233G HS BK-102連接器 零件裝置其它產(chǎn)品
PA66美國巴斯夫8233G HS BK-102連接器 零件裝置
PA66美國巴斯夫 8232G HS FR 熱穩(wěn)定劑 阻燃
PA66美國巴斯夫8232G HS FR BK 耐化學性良好 耐磨蝕性,良好
PA66美國巴斯夫8231G HS BK-106耐化學性良好 耐磨蝕性,良好
PA66美國巴斯夫 8231G HS BK-10低粘度 剛性,良好 高強度
PA66美國巴斯夫 8231G HS低粘度 剛性,良好 高強度
PA66美國巴斯夫 8230GHS 低粘度 剛性,良好 高強度
PA66美國巴斯夫1003-11 NF2001流動性高 熱穩(wěn)定性
PA66美國巴斯夫1000-11 NF2001流動性高 熱穩(wěn)定性
PA66美國Nylene 4114-G13 HS 抗撞擊性,高 耐熱性