PC基礎創新塑料(南沙)HF1140-111 FDA 食品接觸, 未評
: 本公司可以免費提供物性SGS MDS ROHS MSDS UL等證書產品說明 | |
Ideal for disposables/short life cycles. Good clarity, heat resistance, property retention and dimensional stability. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HP1. | |
總體 | |
材料狀態 | 已商用:當前有效 |
資料 1 | Technical Datasheet |
UL 黃卡 2 | E121562-220945 |
搜索 UL 黃卡 | SABIC Innovative PlasticsLEXAN™ |
供貨地區 | 北美洲 |
性能特點 | 尺寸穩定性良好耐熱性,中等食品接觸的合規性一次性中等透明度 |
機構評級 | FDA 食品接觸, 未評級 |
加工方法 | 注射成型 |
多點數據 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831)Elastic Modulus vs Temperature (ASTM D4065)Flexural DMA (ASTM D4065)Shear DMA (ASTM D4065)Specific Heat vs. Temperature (ASTM D3417)Tensile Creep (ASTM D2990)Tensile FatigueTensile Stress vs. Strain (ASTM D638)Thermal Conductivity vs. Temperature (ASTM E1530)Viscosity vs. Shear Rate (ASTM D3835) |
物理性能 | 額定值 | 單位制 | 測試方法 |
比重 | ASTM D792 | ||
-- | 1.20 | ||
-- | 1.19 | g/cm3 | |
特定體積 | 23.0 | in3/lb | ASTM D792 |
熔流率 (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
溶化體積流率(MVR) (300°C/1.2 kg) | 1.40 | in3/10min | ISO 1133 |
收縮率 - 流動 (0.126 in) | 0.0050 到 0.0070 | in/in | Internal Method |
吸水率 | ASTM D570 | ||
24 hr | 0.15 | % | |
平衡, 73°F | 0.35 | % | |
平衡, 212°F | 0.58 | % | |
硬度 | 額定值 | 單位制 | 測試方法 |
洛氏硬度 | ASTM D785 | ||
M 計秤 | 70 | ||
R 計秤 | 118 |
機械性能 | 額定值 | 單位制 | 測試方法 |
拉伸模量 | |||
-- 3 | 344000 | psi | ASTM D638 |
-- | 341000 | psi | ISO 527-2/1 |
抗張強度 | |||
屈服 4 | 8990 | psi | ASTM D638 |
屈服 | 9140 | psi | ISO 527-2/50 |
斷裂 4 | 9430 | psi | ASTM D638 |
斷裂 | 7250 | psi | ISO 527-2/50 |
伸長率 | |||
屈服 4 | 6.0 | % | ASTM D638 |
屈服 | 6.0 | % | ISO 527-2/50 |
斷裂 4 | 120 | % | ASTM D638 |
斷裂 | 70 | % | ISO 527-2/50 |
彎曲模量 | |||
1.97 in 跨距 5 | 334000 | psi | ASTM D790 |
-- 6 | 334000 | psi | ISO 178 |
彎曲強度 | |||
-- 6, 7 | 13100 | psi | ISO 178 |
屈服, 1.97 in 跨距 5 | 13500 | psi | ASTM D790 |
抗泰伯磨耗 (1000 Cycles, 1000 g, CS-17 轉輪) | 10.0 | mg | ASTM D1044 |
沖擊性能 | 額定值 | 單位制 | 測試方法 |
簡支梁缺口沖擊強度 8 | ISO 179/1eA | ||
-22°F | 4.8 | ft·lb/in2 | |
73°F | 5.7 | ft·lb/in2 | |
懸壁梁缺口沖擊強度 | |||
Natural, Tints | 12 | ft·lb/in | ASTM D256 |
73°F | 12 | ft·lb/in | ASTM D256 |
-22°F 9 | 4.8 | ft·lb/in2 | ISO 180/1A |
73°F 9 | 5.7 | ft·lb/in2 | ISO 180/1A |
無缺口懸臂梁沖擊 (73°F) | 60 | ft·lb/in | ASTM D4812 |
裝有測量儀表的落鏢沖擊 (73°F, Energy at Peak Load) | 478 | in·lb | ASTM D3763 |
落錘沖擊 (73°F) | 1500 | in·lb | ASTM D3029 |
拉伸沖擊強度 10 | 180 | ft·lb/in2 | ASTM D1822 |
熱性能 | 額定值 | 單位制 | 測試方法 |
熱變形溫度 | |||
66 psi, 未退火, 0.252 in | 279 | °F | ASTM D648 |
66 psi, 未退火, 3.94 in 跨距 11 | 271 | °F | ISO 75-2/Be |
264 psi, 未退火, 0.126 in | 259 | °F | ASTM D648 |
264 psi, 未退火, 0.252 in | 259 | °F | ASTM D648 |
264 psi, 未退火, 3.94 in 跨距 11 | 250 | °F | ISO 75-2/Ae |
維卡軟化溫度 | |||
-- | 282 | °F | ISO 306/B50 |
-- | 284 | °F | ISO 306/B120 |
Ball Pressure Test (257°F) | Pass | IEC 60695-10-2 | |
線形膨脹系數 - 流動 | |||
-40 到 203°F | 0.000038 | in/in/°F | ASTM E831 |
73 到 176°F | 0.000039 | in/in/°F | ISO 11359-2 |
比熱 | 0.299 | Btu/lb/°F | ASTM C351 |
導熱系數 | |||
-- | 1.3 | Btu·in/hr/ft2/°F | ASTM C177 |
-- | 1.4 | Btu·in/hr/ft2/°F | ISO 8302 |
RTI Elec | 266 | °F | UL 746 |
RTI Imp | 266 | °F | UL 746 |
RTI Str | 266 | °F | UL 746 |
電氣性能 | 額定值 | 單位制 | 測試方法 |
表面電阻率 | > 1.0E+15 | ohm | IEC 60093 |
體積電阻率 | |||
-- | > 1.0E+17 | ohm·cm | ASTM D257 |
-- | > 1.0E+15 | ohm·cm | IEC 60093 |
介電強度 | |||
0.126 in, in Air | 380 | V/mil | ASTM D149 |
0.126 in, 在油中 | 430 | V/mil | IEC 60243-1 |
介電常數 | |||
50 Hz | 3.17 | ASTM D150 | |
60 Hz | 3.17 | ASTM D150 | |
1 MHz | 2.96 | ASTM D150 | |
50 Hz | 2.70 | IEC 60250 | |
60 Hz | 2.70 | IEC 60250 | |
1 MHz | 2.70 | IEC 60250 | |
耗散因數 | |||
50 Hz | 0.00090 | ASTM D150 | |
60 Hz | 0.00090 | ASTM D150 | |
1 MHz | 0.010 | ASTM D150, IEC 60250 | |
50 Hz | 0.0010 | IEC 60250 | |
60 Hz | 0.0010 | IEC 60250 | |
相比耐漏電起痕指數(CTI) | PLC 2 | UL 746 | |
高電弧燃燒指數(HAI) | PLC 1 | UL 746 | |
高電壓電弧起痕速率 (HVTR) | PLC 2 | UL 746 | |
熱絲引燃 (HWI) | PLC 2 | UL 746 | |
可燃性 | 額定值 | 單位制 | 測試方法 |
UL 阻燃等級 (0.0429 in) | V-2 | UL 94 | |
極限氧指數 | 25 | % | ISO 4589-2 |
光學性能 | 額定值 | 單位制 | 測試方法 |
折射率 | 1.586 | ASTM D542 | |
透射率 (100 mil) | 88.0 | % | ASTM D1003 |
霧度 (100 mil) | 1.0 | % | ASTM D1003 |
注射 | 額定值 | 單位制 | |
干燥溫度 | 250 | °F | |
干燥時間 | 3.0 到 4.0 | hr | |
干燥時間,zui大 | 48 | hr | |
建議的zui大水分含量 | 0.020 | % | |
建議注入量 | 40 到 60 | % | |
螺筒后部溫度 | 480 到 520 | °F | |
螺筒中部溫度 | 500 到 540 | °F | |
螺筒前部溫度 | 520 到 560 | °F | |
射嘴溫度 | 510 到 550 | °F | |
加工(熔體)溫度 | 520 到 560 | °F | |
模具溫度 | 160 到 200 | °F | |
背壓 | 50.0 到 100 | psi | |
螺桿轉速 | 40 到 70 | rpm | |
排氣孔深度 | 0.0010 到 0.0030 | in |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PC基礎創新塑料(南沙)HF1140-111 FDA 食品接觸, 未評其它產品
PC基礎創新塑料(南沙)HF1140-111 FDA 食品接觸, 未評
PC基礎創新塑料(南沙)HF1130R 耐熱性,高
PC基礎創新塑料(南沙)HF1130 耐熱性,高
PC基礎創新塑料(南沙)HF1130 耐熱性,高
PC基礎創新塑料(南沙)HF1130-111 耐熱性,高
PC基礎創新塑料(南沙)HF1130 WH8D312XL 電氣性能與可燃性
PC基礎創新塑料(南沙)HF1110R薄壁部件 鏡頭
PC基礎創新塑料(南沙)HF1110-111薄壁部件 鏡頭
PC基礎創新塑料(南沙) HF1110R 薄壁部件 鏡頭
PC基礎創新塑料(南沙) HF1110R 光學數據存儲