優勢說明:PA66吸水量:每1%吸水量體積增加0.003in,在50%的相對濕度,23℃的氣溫吸水量是2.5%。收縮率為2.25%,比重1.14G/CM3詳細說明:
1.PA66吸水量:每1%吸水量體積增加0.003in,在50%的相對濕度,23℃的氣溫吸水量是2.5%。收縮率為2.25%,比重1.14G/CM3
: 本公司可以免費提供各種材料認
證
產品說明 | |
Vydyne® R533T is a translucent 33% glass reinforced heat stabilized Nylon 66 product specifically designed for use in power steering reservoirs and other applications where chemical resistance, whiteness and transmittance are required. Vydyne R533T is a member of a wide range of glass reinforced resins supplied by Ascend Performance Materials. Other glass fiber loadings available from Ascend Performance Materials include 13% and 43%. Vydyne R533T resins have tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption, and part weight are key advantages of Vydyne glass reinforced Nylon 6,6 resins over aluminum and/or zinc die cast parts. | |
總體 | |
材料狀態 | 已商用:當前有效 |
資料 1 | Processing (English)Technical Datasheet (English) |
搜索 UL 黃卡 | Ascend Performance Materials LLC.Vydyne® |
供貨地區 | 北美洲歐洲亞太地區 |
填料/增強材料 | 玻璃纖維增強材料, 33% 填料按重量 |
添加劑 | 熱穩定劑 |
性能特點 | 高拉伸強度耐化學性良好熱穩定性 |
用途 | 金屬置換汽車的發動機罩下的零件 |
機構評級 | ASTM D 4066 PA 112G35FED L-P-410AMIL M-20693B |
外觀 | 半透明 |
形式 | 顆粒料 |
加工方法 | 注射成型 |
物理性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
密度 | 1.40 | -- | g/cm3 | ISO 1183 |
收縮率 | ISO 294-4 | |||
橫向流量: 73°F, 0.0787 in | 0.90 | -- | % | |
流量: 73°F, 0.0787 in | 0.40 | -- | % | |
吸水率 | ISO 62 | |||
73°F, 24 hr | 0.80 | -- | % | |
平衡, 73°F, 50% RH | 1.8 | -- | % |
機械性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
拉伸模量 (73°F) | 1.48E+6 | 1.15E+6 | psi | ISO 527-2 |
拉伸應力 (斷裂, 73°F) | 30500 | 21800 | psi | ISO 527-2 |
拉伸應變 (斷裂, 73°F) | 4.0 | 6.0 | % | ISO 527-2 |
彎曲模量 (73°F) | 1.38E+6 | 943000 | psi | ISO 178 |
彎曲強度 (73°F) | 42100 | 29700 | psi | ISO 178 |
泊松比 | 0.41 | -- | ISO 527-2 | |
沖擊性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
簡支梁缺口沖擊強度 | ISO 179 | |||
-40°F | 3.8 | -- | ft·lb/in2 | |
73°F | 5.7 | -- | ft·lb/in2 | |
簡支梁缺口沖擊強度 | ISO 179 | |||
-40°F | 無斷裂 | -- | ||
73°F | 無斷裂 | -- | ||
懸壁梁缺口沖擊強度 (73°F) | 5.7 | -- | ft·lb/in2 | ISO 180 |
熱性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
熱變形溫度 | ||||
66 psi, 未退火 | 486 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 455 | -- | °F | ISO 75-2/A |
溶融溫度(DSC) | 507 | -- | °F | ISO 3146 |
線形膨脹系數 | ASTM D696 | |||
流動: 73 到 131°F, 0.0787 in | 0.000013 | -- | in/in/°F | |
橫向: 73 到 131°F, 0.0787 in | 0.000026 | -- | in/in/°F |
電氣性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
體積電阻率 (0.118 in) | 3.0E+15 | -- | ohm·cm | IEC 60093 |
耐電強度 2 (73°F, 0.118 in) | 330 | -- | V/mil | IEC 60243-1 |
漏電起痕指數 (0.118 in) | 400 到 599 | -- | V | IEC 60112 |
光學性能 | 干燥 | 調節后的 | 單位制 | 測試方法 |
透射率 | 23.0 | -- | % | ASTM D1003 |
注射 | 干燥 | 單位制 | |
干燥溫度 | < 158 | °F | |
干燥時間 | 1.0 到 3.0 | hr | |
建議注入量 | 40 到 80 | % | |
建議的zui大回制料比例 | 25 | % | |
螺筒后部溫度 | 536 到 590 | °F | |
螺筒中部溫度 | 536 到 590 | °F | |
螺筒前部溫度 | 536 到 590 | °F | |
射嘴溫度 | 536 到 590 | °F | |
加工(熔體)溫度 | 545 到 581 | °F | |
模具溫度 | 149 到 203 | °F | |
注塑溫度 | 7980 到 20300 | psi | |
注射速度 | 快速 | ||
保壓 | 7980 到 20300 | psi | |
背壓 | 29.0 到 145 | psi | |
螺桿轉速 | 60 到 120 | rpm | |
合模力 | 1.9 到 4.5 | tons/in2 | |
墊層 | 0.118 到 0.252 | in | |
注射說明 | |||
Injection Time: <1 to 2.5 sec |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA66美國首諾 R533T高拉伸強度 耐化學性良好 熱穩定性其它產品
PA66美國首諾 R533T高拉伸強度 耐化學性良好 熱穩定性
PA66美國首諾 R533H經潤滑 良好的流動性
PA66美國首諾 R533 T玻璃纖維增強材料, 33% 潤滑劑
PA66美國首諾 R533H BAT玻璃纖維增強材料, 33% 潤滑劑
PA66美國首諾 R513H良好的流動性 耐化學性良好 耐汽油性
PA66美國首諾 R513H BK良好的流動性 耐化學性良好 耐汽油性
PA66美國首諾 R513H BK玻璃纖維增強材料, 13% 填料按重量
PA66美國首諾 R-220 礦物填料, 40% 填料按重量
PA66美國首諾 R-220齒輪 動力/其它工具
PA66美國首諾 R-220剛性,汽車外部零件 凸輪