產品說明 | |
Ultramid HPN 9233G HS BK-102 is a heat stabilized, pigmented black, 33% glass reinforced PA6 injection molding grade resin in the High Productivity Nylon Series developed for improved cycle times while maintaining excellent properties. It exhibits high strength, rigidity and heat resistance. Surface appearance has been improved, cycle times reduced and creep resistance retained. This heat stabilizer version extends the retention of mechanical properties at elevated temperatures while maintaining excellent chemical resistance to greases, oils and hydrocarbons. Ultramid HPN 9233G HS BK-102 is generally recommended for applications such as window locks, valve bodies, chair shells, door and window hardware, connectors, switch components, relay parts, terminal blocks, power tool housings, gears, chainsaws, blowers, trimmer housings and automotive housings. | |
總體 | |
材料狀態 | 已商用:當前有效 |
資料 1 | Processing - Injection Molding (English)Processing - Injection Molding Cooling Times (English)Technical Datasheet - ASTM (English)Technical Datasheet - ISO (English) |
UL 黃卡 2 | E36632-231189 |
搜索 UL 黃卡 | BASF CorporationUltramid® |
供貨地區 | 北美洲 |
添加劑 | 沖擊調節器熱穩定劑 |
性能特點 | 剛性,高高強度良好的抗蠕變性耐化學性良好耐熱性,高耐碳氫化合物耐油性能耐油脂性能熱穩定性生產階段,快 |
用途 | 動力/其它工具開關連接器汽車領域的應用:型號 |
RoHS 合規性 | RoHS 合規 |
外觀 | 黑色 |
加工方法 | 注射成型 |
物理性能 | 額定值 | 單位制 | 測試方法 |
比重 | |||
-- | 1.39 | ASTM D792 | |
-- | 1.39 | g/cm3 | ISO 1183 |
收縮率 - 流動 (0.125 in) | 0.0030 | in/in | No Standard |
吸水率 | |||
24 hr | 1.1 | % | ASTM D570 |
73°F, 24 hr | 1.1 | % | ISO 62 |
飽和 | 6.4 | % | ASTM D570 |
飽和, 73°F | 6.4 | % | ISO 62 |
平衡, 50% RH | 1.8 | % | ASTM D570 |
平衡, 73°F, 50% RH | 1.8 | % | ISO 62 |
硬度 | 額定值 | 單位制 | 測試方法 |
洛氏硬度 (R 計秤) | 120 | ASTM D785 |
機械性能 | 額定值 | 單位制 | 測試方法 |
抗張強度 (斷裂, 73°F) | 25400 | psi | ASTM D638, ISO 527-2 |
伸長率 (斷裂, 73°F) | 3.0 | % | ASTM D638, ISO 527-2 |
彎曲模量 | |||
73°F | 1.36E+6 | psi | ASTM D790 |
73°F | 1.22E+6 | psi | ISO 178 |
彎曲強度 (73°F) | 38400 | psi | ASTM D790 |
沖擊性能 | 額定值 | 單位制 | 測試方法 |
懸壁梁缺口沖擊強度 | |||
73°F | 1.8 | ft·lb/in | ASTM D256 |
-40°F | 3.3 | ft·lb/in2 | ISO 180 |
73°F | 4.5 | ft·lb/in2 | ISO 180 |
Drop Impact Resistance (73°F) | 3.40 | ft·lb | Internal Method |
熱性能 | 額定值 | 單位制 | 測試方法 |
熱變形溫度 | |||
66 psi, 未退火 | 345 | °F | ISO 75-2/B |
264 psi, 未退火 | 406 | °F | ASTM D648 |
264 psi, 未退火 | 129 | °F | ISO 75-2/A |
熔融峰值溫度 | 428 | °F | ASTM D3418, ISO 3146 |
線形膨脹系數 - 流動 | 0.000021 | in/in/°F | ASTM E831 |
RTI Elec (0.0591 in) | 284 | °F | UL 746 |
RTI Imp (0.0591 in) | 239 | °F | UL 746 |
RTI Str (0.0591 in) | 284 | °F | UL 746 |
電氣性能 | 額定值 | 單位制 | 測試方法 |
體積電阻率 | |||
0.0591 in | > 1.0E+15 | ohm·cm | ASTM D257 |
-- | > 1.0E+15 | ohm·cm | IEC 60093 |
介電強度 (0.0591 in) | 560 | V/mil | ASTM D149 |
可燃性 | 額定值 | 單位制 | 測試方法 |
UL 阻燃等級 (0.0591 in) | HB | UL 94 |
注射 | 額定值 | 單位制 | |
干燥溫度 | 176 | °F | |
干燥時間 | 2.0 到 4.0 | hr | |
建議的zui大水分含量 | 0.10 | % | |
加工(熔體)溫度 | 518 到 563 | °F | |
模具溫度 | 176 到 203 | °F | |
注塑溫度 | 508 到 1810 | psi | |
注射速度 | 快速 |
:何生
:86-
傳真號碼:86-
地址:廣東 東莞市
PA66美國巴斯夫 HPN 9233G HS BK-102耐碳氫化合物 耐油其它產品
PA66美國巴斯夫 HPN 9233G HS BK-102耐碳氫化合物 耐油
PA66美國巴斯夫 8272G HS BK-102
PA66美國巴斯夫 8267G HS BK-106A剛性,良好 高強度
PA66美國巴斯夫 8267G HS BK-106抗彎曲 抗紫外線性能良好
PA66美國巴斯夫 8267G HS BK-102良好的抗蠕變性 良好的流動
PA66美國巴斯夫 8262G HS BK-102低翹曲性 低粘度
PA66美國巴斯夫 8235G HS BK-102玻璃纖維增強材料, 50%
PA66美國巴斯夫 8234G HS低粘度 剛性,高
PA66美國巴斯夫 8234G HS低粘度 剛性,高
PA66美國巴斯夫 8234G HS BK-102耐油性能 耐油脂性能 熱穩