特性備注:易流動(dòng),易脫模,快速固化 重要參數(shù): 成型收縮率:1.14 % 缺口沖擊強(qiáng)度:10 氧指數(shù):26 % 拉伸強(qiáng)度:50 MPa 斷裂伸長(zhǎng)率:35 % 彎曲強(qiáng)度:110 MPa 彎曲模量:2900 MPa
產(chǎn)品說明 | |
Ultramid 8267G HS BK-106A is a heat stabilized, weather resistant, 40% mineral and glass fiber reinforced PA6 injection molding compound with improved UV resistance and sink mark resistance. The combination of mineral and glass fibers result in a high performance, low warp and cost effective engineering thermoplastic. It exhibits high strength, good UV resistance, rigidity and good heat distortion temperatures. It has a relatively high resistance to creep under load. The heat stabilizer system extends its retention of properties at elevated temperatures. It has good chemical resistance to greases, oils and hydrocarbons. | |
總體 | |
材料狀態(tài) | 已商用 |
資料 1 | Processing - Injection Molding (English)Processing - Injection Molding Cooling Times (English)Technical Datasheet - ASTM (English)Technical Datasheet - ISO (English) |
搜索 UL 黃卡 | BASF CorporationUltramid® |
供貨地區(qū) | 北美洲 |
填料/增強(qiáng)材料 | 玻璃纖維增強(qiáng)材料, 15% 填料按重量礦物填料, 25% 填料按重量 |
添加劑 | 熱穩(wěn)定劑 |
性能特點(diǎn) | 半結(jié)晶尺寸穩(wěn)定性良好低翹曲性低粘度剛性,良好高強(qiáng)度抗彎曲抗紫外線性能良好可加工性,良好良好的表面光潔度良好的抗熱老化性良好的抗蠕變性良好的流動(dòng)性耐化學(xué)性良好耐磨蝕性,良好熱穩(wěn)定性 |
用途 | 把手車輪汽車領(lǐng)域的應(yīng)用:室外應(yīng)用 |
機(jī)構(gòu)評(píng)級(jí) | ULC Unspecified Rating |
RoHS 合規(guī)性 | RoHS 合規(guī) |
外觀 | 黑色 |
形式 | 顆粒料 |
加工方法 | 注射成型 |
物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
比重 | |||
-- | 1.48 | ASTM D792 | |
-- | 1.48 | g/cm3 | ISO 1183 |
-- | 0.0535 | lb/in3 | ISO 1183 2 |
收縮率 - 流動(dòng) (0.125 in) | 0.0040 | in/in | ASTM D955 |
吸水率 | |||
24 hr | 0.90 | % | ASTM D570 |
73°F, 24 hr | 0.90 | % | ISO 62 |
飽和 | 5.7 | % | ASTM D570, ISO 62 2 |
飽和, 73°F | 5.7 | % | ISO 62 |
平衡, 50% RH | 1.6 | % | ASTM D570 |
平衡, 73°F, 50% RH | 1.6 | % | ISO 62 |
平衡 | 1.6 | % | ISO 62 2 |
硬度 | 額定值 | 單位制 | 測(cè)試方法 |
洛氏硬度 (R 計(jì)秤) | 121 | ASTM D785 |
機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
拉伸模量 | |||
73°F | 1.22E+6 | psi | ISO 527-2 |
-- | 1.22E+6 | psi | ISO 527-2 2 |
抗張強(qiáng)度 | |||
斷裂, 73°F | 17400 | psi | ASTM D638 |
斷裂, 73°F | 17100 | psi | ISO 527-2 |
斷裂 | 17100 | psi | ISO 527-2 2 |
伸長(zhǎng)率 | |||
斷裂, 73°F | 2.0 | % | ASTM D638, ISO 527-2 |
斷裂 | 2.0 | % | ISO 527-2 2 |
彎曲模量 | |||
73°F | 1.04E+6 | psi | ASTM D790 |
73°F | 1.06E+6 | psi | ISO 178 |
彎曲強(qiáng)度 | |||
73°F | 27600 | psi | ASTM D790 |
73°F | 24700 | psi | ISO 178 |
沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 | |||
-22°F | 2.4 | ft·lb/in2 | ISO 179 |
73°F | 2.6 | ft·lb/in2 | ISO 179 |
-22°F | 2.38 | ft·lb/in2 | ISO 179/1eA 2 |
73°F | 2.62 | ft·lb/in2 | ISO 179/1eA 2 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 (73°F) | 21 | ft·lb/in2 | ISO 179 |
懸壁梁缺口沖擊強(qiáng)度 (73°F) | 1.0 | ft·lb/in | ASTM D256 |
熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
熱變形溫度 | |||
66 psi, 未退火 | 419 | °F | ISO 75-2/B |
66 psi | 419 | °F | ISO 75-2 2 |
264 psi, 未退火 | 392 | °F | ISO 75-2/A |
264 psi | 392 | °F | ISO 75-2 2 |
熔融峰值溫度 | 428 | °F | ASTM D3418, ISO 3146 |
線形膨脹系數(shù) - 流動(dòng) | 0.000017 | in/in/°F | ASTM E831 |
注射 | 額定值 | 單位制 | |
干燥溫度 | 176 | °F | |
干燥時(shí)間 | 2.0 到 4.0 | hr | |
建議的zui大水分含量 | 0.10 | % | |
加工(熔體)溫度 | 518 到 563 | °F | |
模具溫度 | 176 到 203 | °F | |
注塑溫度 | 508 到 1810 | psi | |
注射速度 | 快速 |
:何生
:86-
傳真號(hào)碼:86-
地址:廣東 東莞市
PA6德國(guó)巴斯夫 8267G HS BK-106A其它產(chǎn)品
PA6德國(guó)巴斯夫 8267G HS BK-106抗彎曲 抗紫外線性能良好
PA6德國(guó)巴斯夫 8267G HS BK-106A
PA6德國(guó)巴斯夫 8267GHS
PA6德國(guó)巴斯夫 8253HS BK102 管道 緊固件
PA6德國(guó)巴斯夫 8233GH6
PA6德國(guó)巴斯夫 8233G HS BK-102良好的抗熱老化性 良好的抗蠕
PA6德國(guó)巴斯夫 8233G HS BK-106良好的表面光潔度 良好的抗
PA6德國(guó)巴斯夫 8233G HS耐化學(xué)性良好 耐磨蝕性,良好 熱穩(wěn)定性
PA6德國(guó)巴斯夫 8233G耐化學(xué)性良好 耐磨蝕性,良好 熱穩(wěn)定性
PA6德國(guó)巴斯夫 8232G HS FR BK-102 半結(jié)晶 尺寸穩(wěn)定性