Ultem PEI 2212EPR 介紹
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.Ultem PEI 2212EPR 物性表
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D 792 |
Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
Melt Flow | 15 g/10 min @Load 6.60 kg, Temperature 337 °C | 15 g/10 min @Load 14.6 lb, Temperature 639 °F | ASTM D 1238 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D 638 |
Tensile Strength, Yield | 107 MPa | 15500 psi | Type I, 5 mm/min; ASTM D 638 |
Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D 638 |
Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D 638 |
Tensile Modulus | 5.79 GPa | 840 ksi | 5 mm/min; ASTM D 638 |
Flexural Strength | 172 MPa | 24900 psi | brk, 2.6 mm/min, 100 mm span; ASTM D 790 |
Flexural Yield Strength | 172 MPa | 24900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
Flexural Modulus | 5.10 GPa | 740 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
5.51 GPa | 799 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
Izod Impact, Notched | 0.580 J/cm @Temperature 23.0 °C | 1.09 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
Izod Impact, Unnotched | 4.80 J/cm @Temperature 23.0 °C | 8.99 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
Impact Test | 12.0 J @Temperature 23.0 °C | 8.85 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
Electrical Properties | Metric | English | Comments |
Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten, PLC code 5; ASTM D 495 |
Comparative Tracking Index | 100 - 175 V | 100 - 175 V | PLC code 4; UL 746A |
Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | PLC code 1; UL 746A |
High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | surface, PLC code 4; UL 746A |
High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | PLC code 4; UL 746A |
Thermal Properties | Metric | English | Comments |
CTE, linear, Parallel to Flow | 36.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 20.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
CTE, linear, Transverse to Flow | 72.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 40.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
Deflection Temperature at 0.46 MPa (66 psi) | 210 °C @Thickness 3.20 mm | 410 °F @Thickness 0.126 in | unannealed; ASTM D 648 |
212 °C @Thickness 6.40 mm | 414 °F @Thickness 0.252 in | unannealed; ASTM D 648 | |
Deflection Temperature at 1.8 MPa (264 psi) | 205 °C @Thickness 3.20 mm | 401 °F @Thickness 0.126 in | unannealed; ASTM D 648 |
207 °C @Thickness 6.40 mm | 405 °F @Thickness 0.252 in | unannealed; ASTM D 648 | |
Vicat Softening Point | 210 °C | 410 °F | Rate B/50; ASTM D 1525 |
UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | UL 94 |
簡單介紹概述:
PEI(聚醚酰亞胺)具有優良的機械性能、電絕緣性能、耐輻照性能、耐高低溫及耐磨性能,并可透過微波。PEI兼具優良的高溫機械性能和耐磨性,故可用于制造輸水管轉向閥的閥件。由于具有很高的強度、柔韌性和耐熱性,PEI是優良的涂層和成膜材料,能形成適用于電子工業的涂層和薄膜。主要特點 連續工作溫度范圍大(-200-170度*工作),玻璃化溫度與熱變性溫度接近、熔點高達330度 在低溫/高溫下仍保有高機械強度高溫下、高硬度、高抗蠕變性、良好韌性杰出的抗析出性(適合用在利用蒸氣消毒的殺菌室 );不易滋生細菌,常用于食品加工業 高抗輻射性優異、可透過紅外光和微波輻射;電器絕緣性好、良好的電鍍性能 較寬溫度(-200-170度)范圍保持穩定的介電常數和損耗因數不能通過SMT回流焊接測試 主要應用 電子行業:連接件、普通和微型繼電器外殼普通和微型繼電器外殼、電路板、線圈、軟性電路軟性電路、反射鏡、高精度密光纖元件、高溫隔熱板 汽車行業:連接件、高功率車燈和指示燈、控制汽車艙室外部溫度的傳感器、控制空氣和燃料混合物溫度的傳感器,醫療器材等。
PEI 塑膠原料
※美國GE 1000-1000/7101,1010-1000/7001,ATX200,2100,220
產品介紹:
※PEI無定形,具有杰出的耐高溫、高強度、高模量及廣泛的耐化學劑性。 ※天性耐燃,且煙氣排放量低。 3、高的介電常數和損耗因數 耐高溫,高流動
PEI 塑膠原料 (聚醚酰亞胺)
※美國GE:1000;1000F;1000P;1000R;1010;1010F;1000R;1100;1100F;1100R;1110;1110F:8015;D9065;9075; 9076;ATX100;ATX100F;ATX100R;ATX200;ATX200F;ATX200R 2) 日本寶理/日本出光:1140A6,K531A1,6165A4 PEI 美國GE 1100F-2187 PEI 美國GE 1010-7101 PEI 美國GE 2100 PEI 美國GE 2200 PEI 美國GE 2300 PEI 美國GE 1000-1000 PEI 美國GE 1000-7101 PEI 美國GE 1010-1000 PEI 美國GE 2210R-111/7301 PEI 美國GE 2300R-111/7301 PEI 美國GE 2310R-111/7301 PEI 美國GE ATX200F
材料性能表
※注塑 未增強型 標準 1000,1000F,1000P,1000R
※易流動性 1010,1010F,1000R
※加顏料的樹脂 1100,1100F,1100R ,1110,1110F
※中等耐熱性 1285,LTX300A,LTX300B
※增強型 玻璃纖維增強型 2100,2100N,2100R,2110,2110N,2110R,2200,2200R,2210,2210R,2300,2300N,2300R 2310,2310R,2400,2410,2410R
※研磨玻璃纖維增強型 2212,2212R,2312,2313
※玻璃纖維/礦物增強型 3451,3452
※碳纖維增強型 7201,7801
※耐磨性 未增強型 4001 增強型 4000,4211
※抗沖擊性變化 HTX1010F,HTX1050F,HTX2000F,HTX2001F
※耐化學劑性未增強型 CRS5001,CRS5011,CRS5011F,CRS5011R
※增強型 CRS5111,CRS5112,CRS5711,CRS5201,CRS5201R,CRS5211,CRS5211R ,CRS5301 ,CRS5311
※航空樹脂 未增強型 9075,9076 增強型 AR9100,AR9200,AR9300
※混合級 PEI/PCE 混合 ATX100,ATX100F,ATX100R,ATX200,ATX200F,ATX200R
※PEI/PPO 混合 MD133
※擠塑 航空樹脂 8015,D9065
:羅長龍
:
傳真號碼:
地址:中國廣東東莞市樟木頭鎮塑膠原料市場
Ultem PEI 2212EPR其它產品
Ultem PEI 2212
Ultem PEI 2210R
Ultem PEI 2210K
Ultem PEI 2210F
Ultem PEI 2210EPR
Ultem PEI 2200R
Ultem PEI 2200N
Ultem PEI 2200F
Ultem PEI 2200