OK AristoRod™ 13.09是一種適適用于抗蠕變鋼GMAW焊接的0.5Mo合金化實芯焊絲，該抗蠕變鋼與500°C工作溫度下壓力容器與鍋爐管道使用材料的成分相同。OK AristoRod™ 13.09經過伊薩的表面特性(ASC)技術處理，其可將MAG焊接操作提升到全新高度，并且在機器人和自動化焊接中具有的高效性。其特性包括優良的引弧性能；高速送絲和遠距離送絲；較高焊接電流下電弧極其穩定；飛濺少；較低煙塵排放；導電嘴磨損少且焊絲腐蝕防護得到改善。
| 分類: | G 38 0 C1 2Mo, EN ISO 14341-A, Weld Metal, G 46 2 M21 2Mo, EN ISO 14341-A, Weld Metal, G 2Mo, EN ISO 14341-A, Wire Electrode, G MoSi, EN ISO 21952-A, Wire Electrode, G 1M3, EN ISO 21952-B, Wire Electrode, ER70S-A1 (ER80S-G), SFA/AWS A5.28, Wire Electrode |
| 認證: | EN 13479, CE, 42.039.31, DB, III YMS (M21), DNV-GL, 1.2MM, NAKS/HAKC, 10088, VdTüV |
Approvals are based on factory location. Please contact ESAB for more information.
| Alloy Type: | Low alloyed (0.5 % Mo) |
焊縫金屬分析
夏比V型缺口沖擊性能
| 80Ar/20CO2 As welded |
| Impact Value | Testing Temperature | Stress Relieved Testing Temp | Stress Relieved Testing Time |
| 117 J | 20 °C | - | - |
| 75 J | -20 °C | - | - |
| 57 J | -40 °C | - | - |
| 80Ar/20CO2 Stress relieved |
| Impact Value | Testing Temperature | Stress Relieved Testing Temp | Stress Relieved Testing Time |
| 150 J | 20 °C | 620 °C | 15 hr |
| 130 J | 0 °C | 620 °C | 15 hr |
| 95 J | -20 °C | 620 °C | 15 hr |
| 90 J | -40 °C | 620 °C | 15 hr |
Typical Tensile Properties
| 80Ar/20CO2 As welded+ |
| Elongation | Tensile Strength | Yield Strength | Stress Relieved Temperature | Stress Relieved Testing Time |
| 20 % | 570 MPa | 425 MPa | - | - |
| 80Ar/20CO2 As welded |
| Elongation | Tensile Strength | Yield Strength | Stress Relieved Temperature | Stress Relieved Testing Time |
| 26 % | 630 MPa | 515 MPa | - | - |
| 80Ar/20CO2 Stress relieved |
| Elongation | Tensile Strength | Yield Strength | Stress Relieved Temperature | Stress Relieved Testing Time |
| 23 % | 490 MPa | 370 MPa | 620 °C | 15 hr |
| 26 % | 545 MPa | 430 MPa | 620 °C | 15 hr |
熔敷數據
| 安培 | 熔敷率 | 電壓 V | 直徑 | 送絲速度 |
| 40-170 A | 0,4-2,6 kg/h | 16-22 V | 0.8 mm | 2-10,8 m/min |
| 80-280 A | 1-5,4 kg/h | 18-28 V | 1.0 mm | 2,7-14,7 m/min |
| 120-350 A | 1,5-6,6 kg/h | 20-33 V | 1.2 mm | 2,7-12,4 m/min |
| 225-480 A | 3,3-11.6 kg/h | 26-38 V | 1.6 mm | 3,10-12 m/min |