代 號 PART NO. | 螺紋 E THREAD | 軟 管 HOSE BORE | 尺 寸 DIMENSIONS | |||||
公稱內徑 DN | 標號 DASH | A | H | S2 | ||||
20291-12-04 | M12X1.25 | 6 | 4 | 30 | 33.5 | 17 | ||
20291-14-04 | M14X1.5 | 6 | 4 | 30 | 34 | 19 | ||
20291-14-05 | M14X1.5 | 8 | 5 | 33 | 37 | 19 | ||
20291-16-04 | M16X1.5 | 6 | 4 | 30 | 35 | 22 | ||
20291-16-05 | M16X1.5 | 8 | 5 | 34 | 38 | 22 | ||
20291-16-06 | M16X1.5 | 10 | 6 | 35.3 | 40.3 | 22 | ||
20291-18-05 | M18X1.5 | 8 | 5 | 33 | 39 | 24 | ||
20291-18-06 | M18X1.5 | 10 | 6 | 35.75 | 41.3 | 24 | ||
20291-22-06T | M22X1.5 | 10 | 6 | 35.3 | 38.8 | 27 | ||
20291-22-08 | M22X1.5 | 12 | 8 | 41 | 48 | 27 | ||
20291-22-10 | M22X1.5 | 16 | 10 | 57.5 | 53 | 27 | ||
20291-24-08T | M24X1.5 | 12 | 8 | 41 | 45.5 | 30 | ||
20291-27-08T | M27X1.5 | 12 | 8 | 41 | 46 | 32 | ||
20291-27-10 | M27X1.5 | 16 | 10 | 56.5 | 54 | 32 | ||
20291-30-12 | M30X1.5 | 20 | 12 | 66.2 | 63.5 | 36 | ||
20291-36-12T | M36X2 | 20 | 12 | 65.5 | 60 | 41 | ||
20291-36-14T | M36X2 | 22 | 14 | 71.2 | 61 | 41 | ||
20291-39-16T | M39X2 | 25 | 16 | 76.7 | 67.5 | 46 | ||
20291-42-20 | M42X2 | 32 | 20 | 91.5 | 82.5 | 50 | ||
20291-45-20T | M45X2 | 32 | 20 | 91.5 | 78.5 | 55 | ||
20291-52-24T | M52X2 | 40 | 24 | 109.4 | 92 | 60 | ||
20291-60-28T | M60X2 | 45 | 28 | 119.9 | 106.5 | 70 | ||
20291-64-32T | M64X2 | 50 | 32 | 130.95 | 113.3 | 75 |
(1)碳素鋼的性能關鍵在于碳含量。鋼中碳含量提升,鋼的抗壓強度和強度值隨著提升不銹鋼連接頭塑性變形和延展性則隨著減少。(2)硅鍛造碳素鋼中,硅的質量濃度為0.2%-0.45%,這一含量范疇對力學性能的危害并不大。規定硅膠管接頭有一定的含量是為了更好地確保鋼的脫氧,因而,硅在鋼中是有利的原素。(3)硫硫在鋼中是危害原素,它在鋼中關鍵以Fey方式存有。與鐵產生共晶體,其溶點為989度,比鋼的熔點低得多。在鋼的凝上海市液壓軟管固全過程中,硫化物經常在鋼的位錯進行析出,因其抗壓強度低、延性大,液壓接頭大幅度降低了鋼的力學性能且在高溫下非常容易造成熱脆狀況。若鋼液脫氧不太好,含FeC多,則硫化物與鐵及Fe0產生三元共晶體,其溶點更低(約940度),不良影響也更高。硫對鋼的電焊焊接性能也是有不好危害。因而,應在煉鐵時盡可能去除硫。