無色產品在攝氏 23 度時的典型值

測試方法

單位

數值

流變性能

Melt Volume Rate 220 °C/10 kg

ISO 1133

cm³/10 min

7

機械性能

Charpy Notched Impact Strength, 23° C

ISO 179

kJ/m²

17

Charpy Notched Impact Strength, -30° C

ISO 179

kJ/m²

7

Charpy Unnotched, 23° C

ISO 179

kJ/m²

190

Charpy Unnotched, -30° C

ISO 179

kJ/m²

100

Tensile Stress at Yield, 23° C

ISO 527

MPa

51

Tensile Strain at Yield, 23° C

ISO 527

%

3

Tensile Modulus

ISO 527

MPa

2400

Nominal Strain at Break, 23 °C

ISO 527

%

9

Flexural Strength

ISO 178

MPa

72

Flexural Modulus

ISO 178

MPa

2400

Hardness, Ball Indentation

ISO 2039-1

MPa

102

熱性能

Vicat Softening Temperature VST/B/50 (50N, 50°C/h)

ISO 306

°C

106

Vicat Softening Temperature, VST/A/50 (10N, 50°C/h)

ISO 306

°C

115

Heat Deflection Temperature A; (annealed 4 h/80 °C; 1.8 MPa)

ISO 75

°C

99

Heat Deflection Temperature B; (annealed 4 h/80 °C; 0.45 MPa)

ISO 75

°C

107

Coefficient of Linear Thermal Expansion

ISO 11359

10^(-6)/°C

90

Thermal Conductivity

DIN 52612-1

W/(m K)

0.17

電氣性能

Dielectric Strength, Short Time, 1.5 mm

IEC 60243-1

kV/mm

39

Volume Resistivity

IEC 60093

Ohm*m

1E13

Comparative Tracking Index

IEC 60112

V

600

Other Properties

Density

ISO 1183

kg/m³

1050

Moisture Absorption, Equilibrium 23°C/50% RH

ISO 62

%

0.25

Processing

Linear Mold Shrinkage

ISO 294-4

%

0.4 - 0.7

Melt Temperature Range

ISO 294

°C

230 - 260

Mold Temperature Range

ISO 294

°C

30 - 80

Injection Velocity

ISO 294

mm/s

200

Drying Temperature

°C

80

Drying Time

h

2 - 4

Max Service Temperature

°C

85