TPE PELPRENE S6002日本東洋紡供應相關介紹如下:
P-type with high flexibility and high melting point
Item | Method | Unit | P-type with high flexibility and high melting point | |
---|---|---|---|---|
P80C | P95C | |||
Hardness | JIS K6301 | A | 93 | 95 |
ASTM D2240 | D | 38 | 41 | |
Specific Gravity | ASTM D792 | ? | 1.12 | 1.14 |
50% Tensile Modulus | ASTM D638 | MPa | 6.4 | 8.3 |
10% Compression Modulus | ASTM D695 | MPa | 4.2 | 7.6 |
Flexual Modulus | ASTM D790 | MPa | 49 | 74 |
Tensile strength | ASTM D638 | MPa | 26 | 27 |
Tensile elongation | ASTM D638 | % | 600 | 700 |
Tear strength | ASTM D624 | kN/m | 98 | 108 |
IZOD notched impact test | ASTM D256 | J/m | NB | NB |
Taber abrasion | ASTM D1044 | mg/1000c. | 20 | 17 |
Resilience | JIS K6301 | % | 78 | 75 |
Compression set JIS | JIS K6301 | % | 49 | 52 |
Melting point | DSC | ℃ | 203 | 213 |
Vicat softening point | ASTM D1525 | ℃ | 154 | 162 |
Heat deflection temperature | ASTM D648 | ℃ | < 25 | < 25 |
Brittle point | JIS K6301 | ℃ | < -65 | < -65 |
Flammability | UL94 | ? | HB class | HB class |
Coefficient of heat expansion | TMA | 1/K | 17×10?? | 17×10?? |
Dielectric strength | JIS K2111 | MV/m | 20 | 22 |
Volume strength | ASTM D257 | Ω?cm | 12×1012 | 9×1012 |
Moisture absorption | 23℃, 65%RH | % | 0.48 | 0.45 |
Melt flow index | ASTM D1238 | g/10min | 18? | 17? |
Mold shrinkage | Mold 2mm thickness | % | 0.5 | 0.8 |
* Melt flow index a:190℃ b:230℃
The data the description is the popular value, not the guaranteed value.
High-viscous type
Item | Method | Unit | High viscous and high durability type | |
---|---|---|---|---|
P90BD | P46D-01 | |||
Hardness | JIS K6301 | A | 96 | 97 |
ASTM D2240 | D | 57 | 46 | |
Specific Gravity | ASTM D792 | ? | 1.19 | 1.15 |
50% Tensile Modulus | ASTM D638 | MPa | 15.2 | 10.9 |
10% Compression Modulus | ASTM D695 | MPa | 13.3 | 9.6 |
Flexual Modulus | ASTM D790 | MPa | 162 | 110 |
Tensile strength | ASTM D638 | MPa | 31.4 | 31.9 |
Tensile elongation | ASTM D638 | % | 700 | 700 |
Tear strength | ASTM D624 | kN/m | 172 | 165 |
IZOD notched impact test | ASTM D256 | J/m | NB | NB |
Taber abrasion | ASTM D1044 | mg/1000c. | 13 | 10 |
Resilience | JIS K6301 | % | 65 | 70 |
Compression set JIS | JIS K6301 | % | 57 | 55 |
Melting point | DSC | ℃ | 203 | 203 |
Vicat softening point | ASTM D1525 | ℃ | 180 | 153 |
Heat deflection temperature | ASTM D648 | ℃ | 101 | 74 |
Brittle point | JIS K6301 | ℃ | < -65 | < -65 |
Flammability | UL94 | ? | HB class | HB class |
Coefficient of heat expansion | TMA | 1/K | 14×10?? | 17×10?? |
Dielectric strength | JIS K2111 | MV/m | 30 | 25 |
Volume strength | ASTM D257 | Ω?cm | 6×1013 | 4×1013 |
Moisture absorption | 23℃, 65%RH | % | 0.40 | 0.45 |
Melt flow index | ASTM D1238 | g/10min | 3? | 0.5? |
Mold shrinkage | Mold 2mm thickness | % | 1.1 | 0.7 |
* Melt flow index a:190℃ b:230℃
The data the description is the popular value, not the guaranteed value.