東洋紡TPE PELPRENE P40H-05物性表供應相關介紹如下:
Item | Method | Unit | PELPRENE P-Type | ||||
---|---|---|---|---|---|---|---|
P90B | P150B | P280B | E450B | P150M | |||
Hardness | JIS K6301 | A | 96 | 98 | 99 | 99 | 96 |
ASTM D2240 | D | 52 | 57 | 68 | 78 | 50 | |
Specific Gravity | ASTM D792 | ? | 1.19 | 1.23 | 1.26 | 1.28 | 1.19 |
50% Tensile Modulus | ASTM D638 | MPa | 14.7 | 19.6 | 28.4 | 40.3 | 9.8 |
10% Compression Modulus | ASTM D695 | MPa | 13.3 | 19.1 | 35.0 | 39.2 | 9.0 |
Flexual Modulus | ASTM D790 | MPa | 162 | 289 | 494 | 1,267 | 118 |
Tensile strength | ASTM D638 | MPa | 31 | 38 | 37 | 35 | 37 |
Tensile elongation | ASTM D638 | % | 700 | 500 | 500 | 440 | 420 |
Tear strength | ASTM D624 | kN/m | 172 | 177 | 206 | 237 | 142 |
IZOD notched impact test | ASTM D256 | J/m | NB | NB | 78 | 39 | NB |
Taber abrasion | ASTM D1044 | mg/1000c. | 13 | 10 | 8 | 5 | 15 |
Resilience | JIS K6301 | % | 65 | 59 | 55 | ? | 44 |
Compression set JIS | K6301 | % | 57 | 60 | ? | ? | 60 |
Melting point | DSC | ℃ | 203 | 212 | 218 | 222 | 170 |
Vicat softening point | ASTM D1525 | ℃ | 180 | 190 | 199 | 202 | 140 |
Heat deflection temperature | ASTM D648 | ℃ | 101 | 117 | 155 | 161 | 50 |
Brittle point | JIS K6301 | ℃ | < -65 | < -65 | < -60 | < -60 | < -65 |
Flammability | UL94 | ? | HB | HB | HB | HB class | HB class |
Coefficient of heat expansion | TMA | 1/K | 14×10?? | 14×10?? | 14×10?? | 14×10?? | 17×10?? |
Dielectric strength | JIS K2111 | MV/m | 30 | 30 | 30 | 30 | 30 |
Volume strength | ASTM D257 | Ω?cm | 6×1013 | 2×101? | 5×101? | 7×101? | 1×101? |
Moisture absorption | 23℃, 65%RH | % | 0.40 | 0.36 | 0.30 | 0.25 | 0.36 |
Melt flow index | ASTM D1238 | g/10min | 20? | 20? | 13? | 10? | 20? |
Mold shrinkage | Mold 2mm thickness | % | 1.1 | 1.3 | 1.6 | 1.7 | 0.3 |
* Melt flow index a:190℃ b:230℃
The data the description is the popular value, not the guaranteed value.